Abstract
In this study, the output results of 3D printed exterior materials for application to buildings of various shapes are output tests using test specimens, in which 3D printing concrete is cast in a mold and accelerating agents are used to ensure stackability. The unit weight and strength characteristics of the body were analyzed. Compared to the unit weight of concrete placed in the mold, the unit weight of 3D printing concrete using accelerating agents tends to decrease by approximately 3.5% to 5.0%, and the compressive strength is the compressive strength of the concrete placed in the mold. In comparison, the compression strength of the output by 3D printing tended to decrease by approximately 36% to 46%. In the flexural strength, the compressive strength of the output through 3D printing decreased by approximately 36% to 46% compared to the compressive strength of concrete placed in the mold. The impact on the strength characteristics of 3D printed concrete using accelerating agents tended to decrease by approximately 2.0 to 5.8%. Therefore, 3D printing output accelerating agents can be used.
본 연구는 최근 증가하고 있는 건축물의 다양한 외벽 형상에 따라 적용이 가능한 비정형 건축물에의 적용을 위해 3D 프린팅 기법을 적용한 외장재의 제조를 위한 기초 연구로서 진행하였다. 3D 프린팅 외장재의 출력성과 적층성의 확보를 위하여 3D 프린팅 콘크리트를 몰드에 타설한 시험체와 급결제를 사용한 출력물 시험체의 단위중량과 강도특성을 분석하였다. 몰드에 타설한 콘크리트의 단위중량에 비하여 급결제를 사용한 3D 프린팅 콘크리트의 단위중량이 3.5%~5.0% 정도 감소하는 경향을 나타내었고, 압축강도는 몰드에 타설한 콘크리트의 압축강도에 비하여 3D 프린팅을 통한 출력물의 압축강도는 36%~46%정도 감소하는 경향을 나타냈다. 휨강도의 경우 몰드에 타설한 콘크리트의 압축강도에 비하여 3D 프린팅을 통한 출력물의 압축강도는 36%~46%정도 감소하는 경향을 나타냈다. 급결제를 사용한 3D 프린팅 콘크리트의 강도 특성에 관한 영향은 2.0~5.8%정도 감소하는 경향을 나타냈다. 따라서, 3D 프린팅 출력시 급결제의 사용에 따른 강도 특성에 영향은 출력에 의한 강도 특성의 감소 보다 적은 것으로 나타나 3D 프린팅 외장재 제조시 급결제의 사용이 가능한 것으로 판단된다.