Degradation of roller compacted concrete subjected to low-velocity fatigue impacts and salt spray cycles

  • Gao, Longxin (School of Transportation Science and Engineering, Beihang University) ;
  • Lai, Yong (China Airport Construction Group Co.,Ltd.) ;
  • Zhang, Huigui (School of Transportation Science and Engineering, Beihang University) ;
  • Zhang, Jingsong (School of Transportation Science and Engineering, Beihang University) ;
  • Zhang, Wuman (School of Transportation Science and Engineering, Beihang University)
  • 투고 : 2020.08.20
  • 심사 : 2021.11.03
  • 발행 : 2021.11.25

초록

Roller compacted concrete (RCC) used in the island reef airport runway will be subjected to the coupling actions of the fatigue impacts and the salt spray cycles, which will accelerate the deterioration of runway concrete and even threaten the flight safety. A cyclic impact testing machine and a climatic chamber were used to simulate the low-velocity fatigue impact and the salt spray cycles, respectively. The physical properties, the microstructures and the porosity of RCC were investigated. The results show the flexural strength firstly increases and then decreases with the increase of the fatigue impacts and the salt spray cycles. However, the decrease in the flexural strength is significantly earlier than the compressive strength of RCC only subjected to the salt spray cycles. The chlorine, sulfur and magnesium elements significantly increase in the pores of RCC subjected to 30000 fatigue impacts and 300 salt spray cycles, which causes the decrease in the porosity of RCC. The coupling effects of the fatigue impacts and the salt spray cycles in the later period accelerates the deterioration of RCC.

키워드

과제정보

This research is supported by the National Natural Science Foundation of China (Nos. 51678022 and 51978026).

참고문헌

  1. AC 150/5320-6F (2016), Airport Pavement Design and Evaluation, Department of Transportation Advisory Circular, U.S.
  2. ACI 544 (2009), Fiber-Reinforced Concrete, American Concrete Institute, U.S.
  3. Ahn, W. and Reddy, D.V. (2001), "Galvan static testing for the durability of marine concrete under fatigue loading", Cement Concrete Res., 31(3), 343-349. https://doi.org/10.1016/S0008-8846(00)00506-8.
  4. Bonakdar, A. and Mobasher, B. (2010), "Multi-parameter study of external sulfate attack in blended cement materials", Constr. Build. Mater., 24(1), 61-70. https://doi.org/10.1016/j.conbuildmat.2009.08.009.
  5. Brown, P.W. (2002), "Thaumasite formation and other forms of sulfate attack", Cement Concrete Compos., 24(3-4), 301-303. https://doi.org/10.1016/S0958-9465(01)00081-6.
  6. Castro, P., Veleva, L. and Balancan, M. (1997), "Corrosion of reinforced concrete in a tropical marine environment and in accelerated tests", Constr. Build. Mater., 11(2), 75-81. https://doi.org/10.1016/S0950-0618(97)00009-3.
  7. Chen, F., Gao, J.M., Qi, B., Shen, D.M. and Li, L.Y. (2017), "Degradation progress of concrete subject to combined sulfate-chloride attack under drying-wetting cycles and flexural loading", Constr. Build. Mater., 151, 164-171. https://doi.org/10.1016/j.conbuildmat.2017.06.074.
  8. Cojocaru, R., Radu, A. and Budescu, M. (2013), "Modelling of airport rigid pavement for complex configuration of landing gears and for a large spectrum of cement concrete", Int. Res. Eng., 9, 235-242. https://doi.org/10.4028/www.scientific.net/AEF.8-9.235.
  9. Djuric, M., Ranogajec, J., Omorjan, R. and Miletic, S. (1996), "Sulfate corrosion of Portland cement-pure and blended with 30% of fly ash", Cement Concrete Res., 26(9), 1295-1300. https://doi.org/10.1016/0008-8846(96)00127-5.
  10. GB-10125-1997 (1997), Corrosion Tests in Artificial Atmospheres-Salt Spray Tests, People's Republic of China National Standard, China. (in Chinese)
  11. GB-T50082-2009 (2009), Standard for Test Methods of Long-Term Performance and Durability of Ordinary Concrete, People's Republic of China National Standard, China. (in Chinese)
  12. GB/T 16925-1997 (1997), Test Method for Abrasion Resistance of Concrete and Its Products, Ministry of Housing and Urban-Rural Development of the People's Republic of China. (in Chinese)
  13. GJB-1578-1992 (1992), Technical Standard for Airport Pavement Cement Concrete Mix Design, People's Republic of China National Standard, China. (in Chinese)
  14. Gopinath S., Madheswaran C.K., Ramachandra Murthy A., Iyer N.R. and Barkavi T. (2013), "Low and high velocity impact studies on fabric reinforced concrete panels", Comp. Mod. Eng. Sci., 92(2), 151-172. https://doi.org/10.1002/jsid.175.
  15. Kim, Y.Y., Kim, J.M., Bang, J.W. and Kwon, S.J. (2014), "Effect of cover depth, w/c ratio and crack width on half-cell potential in cracked concrete exposed to salt sprayed condition", Constr. Build. Mater., 54, 636-645. https://doi.org/10.1016/j.conbuildmat.2014.01.009.
  16. Li, B., Mao, J.Z., Nawa, T. and Liu, Z.M. (2016), "Mesoscopic chloride ion diffusion model of marine concrete subjected to freeze-thaw cycles", Constr. Build. Mater., 125, 337-351. https://doi.org/ 10.1016/j.conbuildmat.2016.08.052.
  17. Li, P.R., Li, W.G., Yu, T., Qu, F.L. and Tam, V.W.Y. (2020), "Investigation on early-age hydration, mechanical properties and microstructure of seawater sea sand cement mortar", Constr. Build. Mater., 249, 118776. https://doi.org/10.1016/j.conbuildmat.2020.118776.
  18. Liang, L., Gu, Q., Liu, G., Zhang, R. and Jiang, L. (2012), "Using ADAMS to assess dynamic load of pavement during aircraft landing", J. Southwest Jiaotong Univ., 47(3), 502-508. https://doi.org/10.3969/j.issn.0258-2724.2012.03.024.
  19. Liu, H., Huang, H.L., Wu, X.T., Peng, H.X. and Yu, Q.J. (2019), "Effects of external multi-ions and wet-dry cycles in a marine environment on autogenous self-healing of cracks in cement paste", Cement Concrete Res., 120, 198-206. https://doi.org/10.1016/j.cemconres.2019.03.014.
  20. Liu, J., Qiu, Q., Chen, X., Xing, F., Han, N., He, Y. and Ma, Y. (2017), "Understanding the interacted mechanism between carbonation and chloride aerosol attack in ordinary Portland cement concrete", Cement Concrete Res., 95, 217-225. https://doi.org/10.1016/j.cemconres.2017.02.032.
  21. Loukili, A., Roziere, E. and Hachem, R.E. (2009), "Durability of concrete exposed to leaching and external sulphate attacks", Cement Concrete Res., 39(12), 1188-1198. https://doi.org/10.1016/j.cemconres.2009.07.021.
  22. Meira, G.R., Andrade, C. and Alonso, C. (1997), "Durability of concrete structures in marine atmosphere zones: the use of chloride deposition rate on the wet candle as an environmental indicator", Cement Concrete Compos., 32(6), 427-435. https://doi.org/10.1007/s13369-010-0033-5.
  23. MH/T5004-2010 (2010), Specifications for Airport Cement Concrete Pavement Design, Civil Aviation Administration of China.
  24. Niu, D.T., Lu, X.Y. and Miao, Y.Y. (2015), "Diffusion of chloride ions into fatigue-damaged concrete in salt spray environment", J. Xi'an Univ. Ar. Technol., 5, 617. (in Chinese) https://doi.org/10.15986/j.1006-7930.2015.05.001.
  25. Ozaki, S. and Sugata, N. (1998), "Long-term durability of reinforced concrete submerged in the sea", Concrete Under Severe Conditions 2: Environment Loading: Proc. Second Int. Conf. Concrete Under Severe Conditions, CONSEC'98, Tromso, Norway, June.
  26. Perez, G., Calvo, J.G., Carballosa, P., Allegro, V.R., Gaitero, J.J., Erkizia, E. and Guerrero, A. (2015), "Efficiency of an innovative self-healing system in ultra-high-strength concrete under a salt spray test", CONCREEP, 10, 919-928. https://doi.org/10.1061/9780784479346.110.
  27. Pigeon, M. and Malhotra, V.M. (1995), "Frost-resistance of roller-compacted high-volume fly-ash concrete", J. Mater. Civil Eng., 7(4), 208-211. https://doi.org/10.1061/(ASCE)0899-1561(1996)8:4(216).
  28. Piggott, R.W. (1999), "Roller compacted concrete pavements-A study of long-term performance", Portland Cement Assoc., Skokie, IL, USA, R&D serial No. 2261.
  29. Ragab, A.M., Elgammal, M.A., Hodhod, O.A. and Ahmed T.E. (2016), "Evaluation of field concrete deterioration under real conditions of seawater attack", Constr. Build. Mater., 119, 130-144. https://doi.org/10.1016/j.conbuildmat. 2016.05.014.
  30. Murthy, A.R., Palani, G.S., Gopinath, S., Kumar, V.R. and Iyer, N.R. (2013), "An improved concrete damage model for impact analysis of concrete structural components by using finite element method", CMC Comput. Mater., 37(2), 77-96. https://doi.org/10.1109/TCBB.2013.107.
  31. Sahrnaran, M., Lacherni, M. and Hossain, K.M.A. (2009), "Internal curing of engineered cementitious composites for prevention of early age autogenous shrinkage cracking", Cement Concrete Res., 39(l0), 893-901. https://doi.org/10.1016/j.cemconres.2009.07.006.
  32. Saito, M., Ohta, M. and Ishimori, H. (1994), "Chloride permeability of concrete subjected to freeze-thaw damage", Cement Concrete Compos., 16(4), 233-239. https://doi.org/10.1016/0958-9465(94)90035-3.
  33. Silva, M.A.G., Biscaia, H.C. and Marreiros, R. (2013), "Bond-slip on CFRP/GFRP-to-concrete joints subjected to moisture, salt fog and temperature cycles", Compos. Part B. Eng., 55, 374-385. https://doi.org/10.1016/j.compositesb.2013.06.015.
  34. Wang, B., Chen, Y., Fan, H. and Jin, F. (2019), "Investigation of low-velocity impact behaviors of foamed concrete material", Compos. Part B. Eng., 162, 491-499. https://doi.org/10.1016/j.compositesb.2019.01.021.
  35. Wu, Q.L., Yang, Y.H. and Pei, W.W. (2014), "Deterioration damage of concrete in salt spray corrosion and seawater attack", Chin. Concrete Cement Prod., 11, 30-34. (in Chinese)
  36. Xie, J.H., Wei, M.W., Huang, P.Y., Zhang, H. and Chen, P.S. (2019), "Fatigue behavior of the basalt fiber-reinforced polymer/concrete interface under wet-dry cycling in a marine environment", Constr. Build. Mater., 228, 117065. https://doi.org/10.1016/j.conbuildmat.2019.117065.
  37. Yerramala, A. and Ganesh, B.K. (2011), "Transport properties of high-volume fly ash roller compacted concrete", Cement Concrete Compos., 33(10), 1057-1062. https://doi.org/10.1016/j.cemconcomp.2011.07.010.
  38. Yu, H.F., Da, B., Ma, H.Y, Dou, X.M. and Wu, Z.Y. (2020), "Service life prediction of coral aggregate concrete structure under island reef environment", Constr. Build. Mater., 246, 118390. https://doi.org/10.1016/j.conbuildmat.2020.118390.
  39. Zhang, B.S., Zhu, Z.D. and Wu, K.R. (1987), "Fatigue rupture of plain concrete analyzed by fracture mechanics", S.P. Shah S.E. Swartz SEM/RILEM Int. Conf. Fract. Concrete Rock, Houston.
  40. Zhang, J.S. and Zhang, W.M. (2017), "A new equipment and the test method for the impact fatigue test of the concrete", CN201711235189.2, China.
  41. Zhang, W.M, Zhang, N. and Zhou, Y. (2016), "Effect of flexural impact on freeze-thaw and deicing salt resistance of steel fiber reinforced concrete", Mater. Struct., 49, 5161-5168. https://doi.org/10.1617/s11527-016-0851-3.
  42. Zhang, W.M., Chen, S.H and Liu, Y.Z. (2017), "Effect of weight and drop height of hammer on the flexural impact performance of fiber-reinforced concrete", Constr. Build. Mater., 140, 31-35. https://doi.org/10.1016/j.conbuildmat.2017.02.098.
  43. Zhang, W.M., Gong, S. and Zhang, J.S. (2018), "Effect of rubber particles and steel fibers on frost resistance of roller compacted concrete in potassium acetate solution", Constr. Build. Mater., 187, 752-759. https://doi.org/10.1016/j.conbuildmat.2018.07.244.
  44. Zhang, W.M., Sun, W., Zhang, Y.S. and Chen, H.S. (2009), "Degradation of pore structure and microstructures in hardened cement paste subjected to flexural loading and wet-dry cycles in sea water", J. Wuhan Univ. Tech. Mater. Sci. Ed., 24(6), 940-945. https://doi.org/10.1007/s11595-006-6940-1.
  45. Zhang, W.M., Zhang, J.S. and Chen, S.H. (2019), "Frost resistance of roller compacted concrete in airport runway subjected to ethylene glycol solution", Anti-Corros. Meth. Mater., 66(1), 40-44. https://doi.org/10.1108/ACMM-03-2018-1916.
  46. Zhang, W.M., Zhang, Y.C. and Gao, L.X. (2019), "Effect of low-calcium fly ash on sulfate resistance of cement paste under different exposure conditions", Adv. Concrete Constr., 7(3), 175-181. https://doi.org/10.12989/acc.2019.7.3.175.
  47. Zhu D., Gencoglu, M. and Mobasher, B. (2009), "Low velocity flexural impact behavior of AR glass fabric reinforced cement composites", Cement Concrete Compos., 31(6), 379-387. https://doi.org/10.1016/j.cemconcomp.2009.04.011.