Abstract
An Armor Piercing Fin Stabilized Discarding Sabot (APFSDS), which penetrates and sabotages the target by physical energy, consists of a general penetrator using Depleted Uranium (DU) or Tungsten Heavy Alloy (THA) but THA is preferable because of manufacturing and environmental issues. On a THA penetrator, the penetration performance is determined mainly by self-sharpening depending on the hardness and toughness of materials. In particular, the tensile strength and impact strength work as key factors. The correlation coefficient for the penetration performance of the tensile strength was 0.721 and the impact strength was -0.599. The improved penetration performance by additional heat treatment was proven experimentally. Therefore, maintaining elongation over 9 % and tensile strength over 123 kg/㎟ is desirable, and the impact strength should be less than 6.8 kg·m/㎠ for good penetration performance.
송탄통 분리형 날개안정철갑탄은 주로 전차체계에서 물리적인 힘으로 장갑 등과 같은 목표물을 관통 및 파괴하는 탄약으로 주로 열화우라늄 또는 텅스텐 중합금 재료를 사용한 관통자가 사용되고 있으나, 가공 및 환경적 측면 등의 이유로 텅스텐 중합금 관통자가 선호되는 실정이다. 텅스텐 중합금 관통자는 재료의 강도 및 인성에 따라 자기첨예화 효과에 의해 관통능력이 결정되는데, 본 연구에서는 인장강도 및 충격에너지에 가장 큰 영향을 받는 것으로 나타났다. 관통능력에 대한 기계적 특성치들에 대한 상관분석 결과, 관통능력에 대하여 인장강도는 상관계수 0.721의 비례관계를, 충격에너지는 상관계수 -0.599의 반비례관계를 나타냈으며, 추가적인 열처리 공정을 통하여 재료의 충격에너지가 감소시킴으로써 관통능력이 향상되는 사실을 실험적으로 입증하였다. 텅스텐 중합금 관통자의 관통능력을 향상시키기 위해서는 재료의 연신율을 약 9 % 이상으로, 인장강도를 약 123 kg/㎟ 이상으로 유지하는 것이 바람직한 것으로 나타났으며, 특히 충격에너지를 약 6.8 kg·m/㎠ 이하로 제어하는 것이 관통능력 향상에 있어서 가장 중요한 요소로 생각된다.