Abstract
Cards made from PVC and PET materials do not oxidize or decompose readily, so they are generally incinerated or landfilled after use and cause pollution problems, such as environmental hormones and combustion gases during incineration. In addition, there is a problem of environmental pollution because they are discarded as semi-permanent refuse without being decomposed at landfill. This study attempted to solve this problem using polylactic acid (PLA), which is a representative biodegradable material as a substitute material that can solve the issues with these cards. On the other hand, when the thin card core sheet is made from only PLA material, the physical properties of the material are insufficient, such as the low temperature impact strength, high temperature stability, and poor bending properties, so its use is limited. To solve this problem, the compositional ratio of PLA was reviewed, and the optimal biodegradable compound composition was determined through an examination of the compositions, such as crystallization nucleating agents, additives, and nano compound technology. The high functionalization as a biodegradable card was verified through a laminating process using annealing technology.
일반적으로 사용되고 있는 합성수지인 PVC, PET 소재로 이루어진 카드는 쉽게 산화되거나 분해되지 않아서 사용 후에 폐기물로써 소각 또는 매립 처리되어지고 있으며, 소각 과정에서 환경호르몬과 연소가스등의 공해 문제를 일으킨다. 또한 매립 시에는 분해되지 않고 반영구적으로 쓰레기로 남아있어 환경오염을 일으키는 문제점 있다. 본 연구에서는 현재 사용하고 있는 카드의 문제점을 해결할 수 있는 대체 재료로써 대표적인 생분해성 소재인 폴리락트산(PLA : Polylacticacid)을 사용하여 이러한 문제점을 해결하고자 하였다. 그러나 PLA 소재로만 얇은 시트형태의 카드 기재가 만들어질 경우 재료 본래의 물성이 제한되어 저온 충격강도, 고온 안정성, 휨(Bending) 특성 등이 불충분하여 카드로써의 사용범위도 제한될 수밖에 없는 문제점을 가지고 있다. 이를 해결하기 위하여 PLA와 물성보강을 위한 원료의 적절한 배합 조성비를 검토하고, 결정화 핵제 및 첨가제 등의 조성물 검토와 나노컴파운드 기술을 통한 최적의 생분해성 컴파운드 조성물을 제조, 평가 하였다. 또한, 어닐링 (Annealing) 기술을 적용한 라미네이팅 공정을 통해 생분해성 범용 카드로써의 고기능화를 검증하였다.