Abstract
The fracture of a turbine blade of aerospace engine is presented. Although there are a lot of causes and failure modes in blades, the main failure modes are two ways that fracture and fatigue. Degradation of blade material affects most failure modes. Total propagation of failure in this study specifies failure of fracture type. Some section appears fatigue mode. Especially since this study describes analysis of failure for blade in high temperature, it can be a case in point. Analysed blade is Ni super alloy. Investigations of blade are visual inspection, material, microstructure, high temperature stress rupture creep test, analysis and fracture surface, etc. The root cause for fracture was stress rupture due to abnormal thermal environment. Thermal property of Ni super alloy is excellent but if each chemical composition of alloys are different due to change mechanical properties, selection of material is very important.
항공기 엔진을 구성하는 부품 중 하나인 블레이드의 파손에 대해 분석하였다. 블레이드의 파손원인과 그 거동은 다양하지만 크게 일시파단과 피로파손의 두가지 형태로 나뉘어진다. 이 논문에서는 전체 거동은 일시파단으로 진행되고 일부 피로 파손된 블레이드에 대해 기술하였고, 특히 고온에서의 블레이드 손상거동을 분석하므로써 사례의 하나로 제시하고자 한다. 분석한 블레이드는 니켈기 초내열 합금으로 외관, 재질, 미세조직, 고온 크리프 특성, 파단면 형상을 각각의 분석장비를 활용하여 손상원인과 거동을 확인하였고, 원재질에서 재현하였다. 고온에서 니켈 합금은 ${\gamma}^{\prime}$ 형상이 변형되고 조직변형(Alloy Depletion)구간이 관찰되며 재질의 기계적 성질, 물성치 등이 저하되고 연화되어 장시간 운용 시 파손될 수 있다. 니켈합금은 고온특성이 좋으나 함유되는 미량원소에 따라 그 물성치가 다양하므로 니켈합금이라 하여도 그 목적에 맞는 세분화된 소재를 사용해야한다.