Abstract
The objective of this study is to develop a mortar mixture with high workability and adhesive strength for section jacketing in seismic strengthening technology of existing concrete structures. To achieve targeted requirements of the mortars (initial flow exceeding 200 mm, compressive strength of 30MPa, and adhesive strength exceeding 1MPa), step-by-step tests were conducted under the variation of the following mixture parameters: water-to-binder ratio, sand-to-binder ratio, polymer-to-binder ratio, dosage of viscosity agent, and content of ultra-rapid-hardening cement. The adhesive strength of the mortars was also estimated with respect to the various surface treatment states of existing concrete. Based on the test results, the mortar mixture with the polymer-to-binder ratio of 10% and the content of ultra-rapid-hardening cement of 5% can be recommended for the section jacketing materials. The recommended mortar mixture satisfied the targeted requirements as follows: initial flow of 220 mm, high-early strength gain, 28-day compressive strength of 35MPa, and adhesive strength exceeding 1.2MPa.
본 연구의 목적은 기존 콘크리트 건물의 단면확대 내진보강 기술에서 필요한 고유동 고접착성의 보강 모르타르 배합의 개발이다. 보강 모르타르의 목표성능(플로우 220mm 이상, 압축강도 30MPa, 접착강도 1MPa 이상)을 위해 물-결합재비, 잔골재-결합재비, 폴리머-결합재비, 증점제 사용 및 초속경시멘트의 혼입 등을 변수로 단계적으로 배합실험을 수행하였다. 모르타르의 접착강도는 기존 콘크리트의 다양한 면 처리 상태에 따라 평가하였다. 실험결과로부터 단면증설용 보강 모르타르의 배합을 위해 폴리머-결합재비는 10%, 초속경시멘트의 치환율은 5%가 추천될 수 있었는데, 이 배합은 초기 플로우 220 mm, 높은 초기강도 발현, 압축강도 35 MPa 그리고 접착강도 1.2 MPa 이상의 성능을 보였다.