Abstract
In recent years, the early strength of concrete is important in order to shorten the time of form removal at the construction site. The purpose of this study is to analyze the moment of form removal as investigating the amount of cement contents and the physical properties and strength of the concrete according to types of admixture in the curing temperature of $10^{\circ}C$ for concrete of 21 to 27 MPa. As a result, it was found that compressive strength of concrete could not be secured 5 MPa by 36 hours even if the amount of cement contents were increased to $360kg/m^3$ with plain admixture. Also, it was confirmed that the strength improvement rate was excellent when using the accelerating agent with polycarboxylic acid type, and the moment of compressive strength of 5 MPa was estimated at 30 hours.
최근, 건설현장에서는 콘크리트의 거푸집 해체 및 존치기간을 단축하기 위해서는 5MPa의 강도발현이 조기실현 되어야 한다. 한편, 국내의 온도분포를 분석하면 춘/추절기 및 동절기(급열양생 조건)의 경우 양생 온도가 $10^{\circ}C$ 안팎으로 형성되어 콘크리트의 양생에는 매우 열악한 조건이라고 할 수 있으며, 전체 공기에 미치는 영향이 매우 크므로 이를 고려한 콘크리트 품질관리 기술의 요구가 증대되고 있는 현실이다. 이에 콘크리트의 5MPa의 조기강도 발현을 위하여 배합측면에서 W/B의 저하, 단위 시멘트량의 증가 또는 시멘트 분말도의 증가, 고성능 감수제의 사용 등을 고려한 방법들이 주로 검토되고 있으나, 지역적 공급제한, 경제성 등에 의한 실용화가 일부 제한적으로 실시되고 있다. 본 연구에서는 실제 현장의 골조공사에 주로 활용되고 있는 설계기준강도 21~27MPa 범위의 콘크리트를 대상으로 $10^{\circ}C$ 온도조건의 범위에서 단위 시멘트량, 혼화제의 변경에 따른 물성, 강도발현 등을 검토함으로서 거푸집 탈형시기를 분석해보고자 하였다. 실험결과, 일반형 혼화제를 사용한 상태에서 단위 시멘트량 $360kg/m^3$까지 증가하여도 36시간까지 5MPa를 확보할 수 없는 것으로 나타났으며, 결합재 치환을 실시하는 경우에는 48시간에도 5MPa 확보가 어려운 것으로 확인되었다. 또한, 혼화제의 종류에 따라서는 조강형 PC를 사용하는 경우 강도개선율이 우수한 것으로 확인되었으며, 적산온도 평가 결과 5 MPa 발현시기가 30시간으로 추정되었다. 따라서 현장의 배합설계 있어서는 단위시멘트량은 $330kg/m^3$를 기준으로 조강 혼화제의 사용 또는 조강제의 개선에 따른 검토가 이루어져야 할 것으로 판단되었다.