Cyclic fatigue resistance, torsional resistance, and metallurgical characteristics of M3 Rotary and M3 Pro Gold NiTi files

  • 투고 : 2017.09.13
  • 심사 : 2018.02.25
  • 발행 : 2018.05.31

초록

Objectives: To evaluate the mechanical properties and metallurgical characteristics of the M3 Rotary and M3 Pro Gold files (United Dental). Materials and Methods: One hundred and sixty new M3 Rotary and M3 Pro Gold files (sizes 20/0.04 and 25/0.04) were used. Torque and angle of rotation at failure (n = 20) were measured according to ISO 3630-1. Cyclic fatigue resistance was tested by measuring the number of cycles to failure in an artificial stainless steel canal ($60^{\circ}$ angle of curvature and a 5-mm radius). The metallurgical characteristics were investigated by differential scanning calorimetry. Data were analyzed using analysis of variance and the Student-Newman-Keuls test. Results: Comparing the same size of the 2 different instruments, cyclic fatigue resistance was significantly higher in the M3 Pro Gold files than in the M3 Rotary files (p < 0.001). No significant difference was observed between the files in the maximum torque load, while a significantly higher angular rotation to fracture was observed for M3 Pro Gold (p < 0.05). In the DSC analysis, the M3 Pro Gold files showed one prominent peak on the heating curve and 2 prominent peaks on the cooling curve. In contrast, the M3 Rotary files showed 1 small peak on the heating curve and 1 small peak on the cooling curve. Conclusions: The M3 Pro Gold files showed greater flexibility and angular rotation than the M3 Rotary files, without decrement of their torque resistance. The superior flexibility of M3 Pro Gold files can be attributed to their martensite phase.

키워드

참고문헌

  1. Gavini G, Pessoa OF, Barletta FB, Vasconcellos MA, Caldeira CL. Cyclic fatigue resistance of rotary nickel-titanium instruments submitted to nitrogen ion implantation. J Endod 2010;36:1183-1186. https://doi.org/10.1016/j.joen.2010.03.032
  2. Yum J, Cheung GS, Park JK, Hur B, Kim HC. Torsional strength and toughness of nickel-titanium rotary files. J Endod 2011;37:382-386. https://doi.org/10.1016/j.joen.2010.11.028
  3. Parashos P, Messer HH. Rotary NiTi instrument fracture and its consequences. J Endod 2006;32:1031-1043. https://doi.org/10.1016/j.joen.2006.06.008
  4. Pedulla E, Lo Savio F, Boninelli S, Plotino G, Grande NM, Rapisarda E, La Rosa G. Influence of cyclic torsional preloading on cyclic fatigue resistance of nickel - titanium instruments. Int Endod J 2015;48:1043-1050. https://doi.org/10.1111/iej.12400
  5. Cheung GS. Instrument fracture: mechanisms, removal of fragments, and clinical outcomes. Endod Topics 2007;16:1-26. https://doi.org/10.1111/j.1601-1546.2009.00239.x
  6. Pruett JP, Clement DJ, Carnes DL Jr. Cyclic fatigue testing of nickel-titanium endodontic instruments. J Endod 1997;23:77-85. https://doi.org/10.1016/S0099-2399(97)80250-6
  7. Haikel Y, Serfaty R, Bateman G, Senger B, Allemann C. Dynamic and cyclic fatigue of engine-driven rotary nickel-titanium endodontic instruments. J Endod 1999;25:434-440. https://doi.org/10.1016/S0099-2399(99)80274-X
  8. Bryant ST, Thompson SA, Al-Omari MA, Dummer PM. Shaping ability of Profile rotary nickel-titanium instruments with ISO sized tips in simulated root canals: part 1. Int Endod J 1998;31:275-281.
  9. Ounsi HF, Al-Shalan T, Salameh Z, Grandini S, Ferrari M. Quantitative and qualitative elemental analysis of different nickel-titanium rotary instruments by using scanning electron microscopy and energy dispersive spectroscopy. J Endod 2008;34:53-55. https://doi.org/10.1016/j.joen.2007.09.009
  10. Plotino G, Grande NM, Cotti E, Testarelli L, Gambarini G. Blue treatment enhances cyclic fatigue resistance of vortex nickel-titanium rotary files. J Endod 2014;40:1451-1453. https://doi.org/10.1016/j.joen.2014.02.020
  11. Shen Y, Qian W, Abtin H, Gao Y, Haapasalo M. Fatigue testing of controlled memory wire nickel-titanium rotary instruments. J Endod 2011;37:997-1001. https://doi.org/10.1016/j.joen.2011.03.023
  12. United Dental (CN): M3 Rotary brochure [Internet]. Shangai: United Dental; 2016 [cited 2016 Sep 20]. Available from: http://www.m3-endo.com/col.jsp?id=110. (updated 2016 Dec 20).
  13. United Dental (CN): M3 Pro Gold brochure [Internet]. Shangai: United Dental; 2016 [cited 2016 Sep 20]. Available from: http://www.m3-endo.com/col.jsp?id=111. (updated 2016 Dec 20).
  14. Pedulla E, Genovesi F, Rapisarda S, La Rosa GRM, Grande NM, Plotino G, Adorno CG. Effects of 6 single-file systems on dentinal crack formation. J Endod 2017;43:456-461. https://doi.org/10.1016/j.joen.2016.10.038
  15. Gambarini G, Gergi R, Grande NM, Osta N, Plotino G, Testarelli L. Cyclic fatigue resistance of newly manufactured rotary nickel titanium instruments used in different rotational directions. Aust Endod J 2013;39:151-154.
  16. Pedulla E, Plotino G, Grande NM, Scibilia M, Pappalardo A, Malagnino VA, Rapisarda E. Influence of rotational speed on the cyclic fatigue of Mtwo instruments. Int Endod J 2014;47:514-519. https://doi.org/10.1111/iej.12178
  17. Chang SW, Shim KS, Kim YC, Jee KK, Zhu Q, Perinpanayagam H, Kum KY. Cyclic fatigue resistance, torsional resistance, and metallurgical characteristics of V taper 2 and V taper 2H rotary NiTi files. Scanning 2016;38:564-570. https://doi.org/10.1002/sca.21301
  18. Gao Y, Shotton V, Wilkinson K, Phillips G, Johnson WB. Effects of raw material and rotational speed on the cyclic fatigue of ProFile Vortex rotary instruments. J Endod 2010;36:1205-1209. https://doi.org/10.1016/j.joen.2010.02.015
  19. Kramkowski TR, Bahcall J. An in vitro comparison of torsional stress and cyclic fatigue resistance of ProFile GT and Profile GT Series X rotary nickel-titanium files. J Endod 2009;35:404-407. https://doi.org/10.1016/j.joen.2008.12.003
  20. Ha JH, Kim SK, Cohenca N, Kim HC. Effect of R-phase heat treatment on torsional resistance and cyclic fatigue fracture. J Endod 2013;39:389-393. https://doi.org/10.1016/j.joen.2012.11.028
  21. Choi J, Oh S, Kim YC, Jee KK, Kum K, Chang S. Fracture resistance of K3 nickel-titanium files made from different thermal treatments. Bioinorg Chem Appl 2016;2016:6374721.
  22. Shen Y, Zhou H, Zheng Y, Campbell L, Peng B, Haapasalo M. Metallurgical characterization of controlled memory wire nickel-titanium rotary instruments. J Endod 2011;37:1566-1571. https://doi.org/10.1016/j.joen.2011.08.005
  23. de Vasconcelos RA, Murphy S, Carvalho CA, Govindjee RG, Govindjee S, Peters OA. Evidence for reduced fatigue resistance of contemporary rotary instruments exposed to body temperature. J Endod 2016;42:782-787. https://doi.org/10.1016/j.joen.2016.01.025
  24. Kusy RP. A review of contemporary archwires: their properties and characteristics. Angle Orthod 1997;67:197-207.
  25. Ninan E, Berzins DW. Torsion and bending properties of shape memory and superelastic nickel-titanium rotary instruments. J Endod 2013;39:101-104. https://doi.org/10.1016/j.joen.2012.08.010
  26. Shen Y, Qian W, Abtin H, Gao Y, Haapasalo M. Effect of environment on fatigue failure of controlled memory wire nickel-titanium rotary instruments. J Endod 2012;38:376-380. https://doi.org/10.1016/j.joen.2011.12.002
  27. Pedulla E, Lo Savio F, Boninelli S, Plotino G, Grande NM, La Rosa G, Rapisarda E. Torsional and cyclic fatigue resistance of a new nickel-titanium instrument manufactured by electrical discharge machining. J Endod 2016;42:156-159. https://doi.org/10.1016/j.joen.2015.10.004
  28. Wu SK, Lin HC, Chou TS. A study of electrical resistivity, internal friction and shear modulus on an aged Ti49Ni51 alloy. Acta Metall Mater 1990;38:95-102. https://doi.org/10.1016/0956-7151(90)90137-6
  29. Peters OA, Barbakow F. Dynamic torque and apical forces of ProFile 0.04 rotary instruments during preparation of curved canals. Int Endod J 2002;35:379-389. https://doi.org/10.1046/j.0143-2885.2001.00494.x
  30. Bahia MG, Buono VT. Decrease in the fatigue resistance of nickel-titanium rotary instruments after clinical use in curved root canals. Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2005;100:249-255. https://doi.org/10.1016/j.tripleo.2004.10.013
  31. Plotino G, Grande NM, Testarelli L, Gambarini G. Cyclic fatigue of Reciproc and WaveOne reciprocating instruments. Int Endod J 2012;45:614-618. https://doi.org/10.1111/j.1365-2591.2012.02015.x
  32. Park SY, Cheung GS, Yum J, Hur B, Park JK, Kim HC. Dynamic torsional resistance of nickel-titanium rotary instruments. J Endod 2010;36:1200-1204. https://doi.org/10.1016/j.joen.2010.02.016

피인용 문헌

  1. Influence of heat treatment on torsional resistance and surface roughness of nickel‐titanium instruments vol.52, pp.11, 2019, https://doi.org/10.1111/iej.13164
  2. Torsional Resistance of Two New Heat Treated Nickel Titanium Rotary Instruments: An in Vitro Evaluation vol.20, pp.None, 2018, https://doi.org/10.1590/pboci.2020.156
  3. Assessment of Real-Time Operative Torque during Nickel-Titanium Instrumentation with Different Lubricants vol.10, pp.18, 2020, https://doi.org/10.3390/app10186201
  4. A New Device to Test the Bending Resistance of Mechanical Endodontic Instruments vol.10, pp.20, 2020, https://doi.org/10.3390/app10207215
  5. Impact of Peracetic Acid on the Dynamic Cyclic Fatigue of Heat-Treated Nickel-Titanium Rotary Endodontic Instrument vol.2021, pp.None, 2021, https://doi.org/10.1155/2021/6676005
  6. Influence of shaft length on torsional behavior of endodontic nickel-titanium instruments vol.109, pp.3, 2018, https://doi.org/10.1007/s10266-020-00572-2