Abstract
The changes in the mechanical properties according to the width of the tool shoulder, rotation speed and moving speed in friction stir welding (FSW) are evaluated using Al 6061-T6. The results indicated that the tensile strength value increases with increasing rotation speed. The higher the moving speed of the tool shoulder, the lower the tensile strength, regardless of the tool type. A higher tensile strength value was generally obtained with a tool shoulder diameter of 12mm (TSD12) than with 8mm. When the moving and rotation speeds exceed a limiting value, a stabilization stage is reached, in which (the tool shoulder diameter?) no longer affects the material properties. At a tool shoulder diameter of 8mm (TSD8), the material properties are decreased and the mixture of material in the welding area is incomplete in comparison with the tool type of TSD12. The tensile strength value is decreased at a rotation speed of 1500 rpm. As a result, a rotation speed higher than the threshold value is needed in order for and the transition temperature to be reached, which allows the complete mixing of the material in the welding area.
Al 6061-T6를 사용하여 마찰교반 용접 시 회전 툴 숄더의 너비부의 넓이와 회전 속도, 이동속도의 변화에 따른 물성의 변화에 대하여 평가되었다. FSW 공정의 접합 변수에 따라 인장시험을 수행하기 위하여 KS B 0801 5호에 따라 시험편을 제작하여 마찰교반 용접을 시행하였다. 마찰교반 용접이 된 시험편의 기계적 특성을 평가하기 위해 Instron 인장시험기를 사용하여 1mm/min의 시험 속도로 인장시험을 시행했다. 평가결과, 인장강도는 회전 속도가 증가함에 증가 하였다. 툴 숄더의 이동 속도가 빠를수록 툴 유형에 관계없이 인장강도는 감소하였다. 툴 숄더 직경 12 mm (TSD12) 의 인장 강도 값은 일반적으로 8mm 보다 높게 나타났다. 이동 속도와 회전하는 속도가 한계 값을 초과하면 재료의 특성에 영향을 주지 않고 안정화 단계에 도달한다. 툴 숄더 직경 8mm (TSD8) 는 TSD12 유형의 공구와 비교하여 재료 특성이 감소하고 용접 영역에서 재료가 완전히 혼합되지 않는다. 인장 강도 값은 모든 회전 속도 1500 rpm에서 상대적으로 감소한다. 이동 속도가 낮을수록 같은 회전수에서 재료의 혼합될 수 있는 양이 많으므로 인장강도값이 높게 나타난다. 결과적으로 용접 영역에서 재료를 완전히 혼합하고 전이 온도에 도달하기 위해서는 임계값을 초과하는 회전 속도가 필요하다.