Electrical Properties of Co- and Cu-Doped Nickel Manganite System Thick Films for Infrared Detectors

  • Lee, Dong-Jin (Engineering Research Institute, Department Materials Engineering and Convergence Technology, Gyeongsang National University) ;
  • Lee, Sung-Gap (Engineering Research Institute, Department Materials Engineering and Convergence Technology, Gyeongsang National University) ;
  • Kim, Kyeong-Min (Engineering Research Institute, Department Materials Engineering and Convergence Technology, Gyeongsang National University) ;
  • Kwon, Min-Su (Engineering Research Institute, Department Materials Engineering and Convergence Technology, Gyeongsang National University)
  • Received : 2017.05.24
  • Accepted : 2017.07.11
  • Published : 2017.10.25

Abstract

$Ni_{0.79}Co_{0.15-x}Cu_xMn_{2.06}O_4$ ($0{\leq}x{\leq}0.09$) thick films were fabricated using the conventional solid-state reaction method and screen-printing method. Structural and electrical properties of specimens based on the amount of Cu were observed in order to investigate their applicability in the infrared detector. All specimens showed a single spinel phase with a homogeneous cubic structure. As the amount of Cu increased, the average grain size increased and was found to be approximately $5.01{\mu}m$ for the $Ni_{0.79}Co_{0.06}Cu_{0.09}Mn_{2.06}O_4$ specimen. The thickness of all specimens was approximately $55{\sim}56{\mu}m$. As Cu content increased, the resistivity and TCR properties at room temperature decreased, and these values for the $Ni_{0.79}Co_{0.06}Cu_{0.09}Mn_{2.06}O_4$ specimen were $502{\Omega}-cm$ and $-3.32%/^{\circ}C$, respectively. The responsivity and noise properties decreased with an increase in Cu content, with the specimen with a Cu content of x=0.09 showing 0.0183 V/W and $5.21{\times}10^{-5}V$, respectively.

Keywords

References

  1. W. Nunley and J. S. Bechtel, Infrared Optoelectronic Devices and Applications (Marcel and Dekker, Inc., United States, 1987) p. 257.
  2. J. Caniou, Passive Infrared Detection Theory and Applications (Kluwer Academic Pub., Netherlands, 1999) p. 1-26.
  3. J. E. Gray, D. P. Butler, and Z. Celik-Butler, Electron. Lett. , 34, 2164 (1998). [DOI: http://dx.doi.org/10.1049/el:19981455]
  4. X. M. Liu, H. J. Fang, and L. T. Liu, Microelectron. J. , 38, 735 (2007). [DOI: https://doi.org/10.1016/j.mejo.2007.04.018]
  5. R. Metz, J. Mater. Sci. , 35, 4705 (2000). [DOI: https://doi.org/10.1023/A:1004851022668]
  6. K. M. Kim, S. G. Lee, and D. J. Lee, Trans. Elec. and Electro. Mat. , 17, 227 (2016). [DOI: http://dx.doi.org/10.4313/TEEM.2016.17.4.227]
  7. E. G. King, A. D. Mah, and L. B. Pankratz, Thermodynamic Properties of Copper and Its Inorganic Compounds (The International Copper Research Assoc. Inc., New York, 1973) p. 257.
  8. C. Drouet, C. Laberty, J.L.G. Fierro, P. Alphonse, and A. Rousset, Int. J. Inorg. Mater. , 2, 419 (2000). [DOI: https://doi.org/10.1016/S1466-6049(00)00047-7]
  9. K. Park and J. K. Lee, Scripta Mater. , 57, 329 (2007). [DOI: http://dx.doi.org/10.1016/j.scriptamat.2007.04.026]
  10. R. Sololewski, Superconducting and Related Oxide: Physics and Nanoengineering III (D. Pavuna and I. Boznovic, San Diego, USA, 1998) p.480. [DOI: http://dx.doi.org/10.1117/12.335897]