Abstract
The most important aspect determining the completeness of aprosthesis is itsmarginal and internal fit. Alloysare processed using a softening/hardening heat treatment methodin order to improve their mechanical, physical properties and polishing properties. To examinehow the heat treatment method affects the marginal and internal fit of the Ni-Cr alloy core,thirty dental stone models of the abutment of the mandibular left molar were manufactured.The Ni-Cr alloy coreswere manufactured by the dipping method for the experiment and dividedinto three groups; A for no heat treatment, B for softening heat treatment and C for hardening heat treatment. The marginal and internal fitsof all of the groups were measured by the silicone replica technique. A statistical analysis was performed using one-way ANOVA(${\alpha}=0.05$) in order to examine whether there is a significant difference in the average values of the marginal and internal fits among the three groups and it was found that themarginal fits (1, 6) were significantly different (p<0.05), but the internal fits (2, 3, 4, 5) were not significantly different (p>0.05). These results show that Ni-Cr alloys should not be processed bythe heat treatmentmethod.However, they need to be confirmed in further clinical application studies.
보철물의 완성도를 평가할 수 있는 요소는 여러 가지가 있으나, 그 중 가장 중요한 하나는 보철물의 적합도이다. 합금은 기계적, 물리적 성질 그리고 연마성 개선을 위해 연화열처리나 경화열처리 과정을 거치는데, 이때의 열처리 방법이 Ni-Cr 합금 core의 변연 및 내면 간격에 어떠한 영향을 미치는지 알아보고자 한다. 실험을 위해 하악 좌측 대구치가 지대치인 석고 모형 30개를 제작하고 dipping법을 이용하여, 3 group(A, B, C)으로 나누어 group당 10개, 총 30개의 Ni-Cr 합금 core를 제작 하였다. 이들을 열처리를 하지 않은 것과 연화, 경화 열처리 방법으로 열처리함에 따라 적합도를 silicone replica technique을 이용하여 측정하였다. 세 집단 간의 평균값에 유의한 차이가 있는지 알아보기 해 독립표본 t-검정으로 분석하였다(${\alpha}=0.05$). 실험 결과 변연 부위(1, 6)에서는 통계적으로 유의한 차이를 보였으나(p<0.05), 나머지 내면 부위(2, 3, 4, 5)에서는 유의한 차이를 보이지 않았다(p>0.05). 이러한 결과로 미루어 볼 때 Ni-Cr 합금은 열처리를 하지 않는 것이 적합도 측면에서 나을 것으로 사료된다. 이에 추가적인 임상적용 연구를 통해 더욱 심도 있는 평가되어야 할 것으로 판단된다.