Abstract
Physical, mechanical and deteriorating properties of Phellodendron amure were investigated. Air dried density located indoor was 0.41 but $0.43g/cm^3$ outdoor. In oven dry shrinkage, T/R ratio for located indoor was 1.40 but 1.32 outdoor. Hygroscopic property at $40^{\circ}C$ with 90% relative humidity was 16.30% for indoor and 15.80% for outdoor. Compressive strength for outdoor conditioned sample was 43.81 MPa but 40.33 MPa for indoor conditioned. Also bending strenght for outdoor conditioned was 84.63 MPa but 68.80 MPa for indoor conditioned. Impact strength was 3.43 and $4.00J/cm^2$ indoor and outdoor, respectively. Hardness at cross-section was 47.92 and 49.20 MPa indoor and outdoor, respectively. With one-year conditioning at indoor or outdoor, there was no significantly different in strength properties, which came from strong resistance for deterioration. Also Phellodendron amure wood showed dimensionally stable raw material based on low T/R ratio.
본 연구는 황벽나무의 물리, 역학적 성질의 특성과 부후성을 조사하였다. 기건밀도는 실내, 외 방치한 목재에서 각각 0.41, $0.43g/cm^3$로 나타났다. 전수축율 시 T/R비는 실내, 외에서 각각 1.40, 1.32로 나타났다. 흡습성은 온도 $40^{\circ}C$ 상대습도 90% 경우 실내, 외에서 각각 16.30, 15.80%로 나타났다. 압축강도는 실내, 외에서 각각 43.81, 40.33 MPa 휨강도는 84.63, 68.80 MPa, 충격강도는 3.43, $4.00J/cm^2$, 경도는 횡단면에서 각각 47.92, 49.20 MPa로 나타났다. 경도는 횡단면에서 각각 47.92, 49.20 MPa로 나타났다. 1년간 실내에 방치한 목재와 실외에 방치한 목재는 부후에 강하고, 또한 T/R비도 낮은 편으로 치수가 안정한 나무로 판단된다.