Abstract
Bulk-type body-centered-tetragonal Fe-Co alloy was synthesised by utilising a conventional alloy preparation technologies, such as melting, solidification, and homogenising treatments, and its magnetic properties were investigated. In the $(Fe_{100-x}Co_x)_{1-y}C_y$ alloy, the composition range, from which single phase body-centered-tetragonal alloy (martensite phase) was obtained, was severely limited: Co content x = 2.5, and C content y = 0.062. Tetragonality(c/a) of the synthesised body-centered-tetragonal $(Fe_{97.5}Co_{2.5})_{0.938}C_{0.062}$ alloy was 1.05. Magnetocrystalline anisotropy constant ($K_1$) of the body-centered-tetragonal $(Fe_{97.5}Co_{2.5})_{0.938}C_{0.062}$ alloy was measured to be $9.8{\times}10^5J/m^3$), which was 3.1 time as high as the pure iron (${\alpha}-Fe$).
합금 제조에 흔히 이용되는 기존의 용해, 응고, 열처리 등의 가공 공정으로 덩치 형태의 체심정방정 구조의 Fe-Co계 합금상을 합성하고, 그 결정학적, 자기적 특성을 조사하였다. $(Fe_{100-x}Co_x)_{1-y}C_y$ 합금에서 체심정방정 구조의 단일상(martensite)이 얻어지는 Co 및 C의 함량은 크게 제한되어, Co의 함량 x = 2.5, C의 함량 y = 0.062로 제한된 조성에서 체심정방정 구조의 단일상 합금이 얻어졌다. 합성된 조성 $(Fe_{97.5}Co_{2.5})_{0.938}C_{0.062}$인 체심정방정 구조의 단일상 합금의 정방성(tetragonality, c/a)은 1.05였으며, 이 합금의 결정자기 이방성 상수, $K_1$ 값은 순수 철(${\alpha}-Fe$)의 $K_1$ 값에 비하면 3.1배 정도 높은 $1.5{\times}10^5J/m^3$였다.