The effect of plasma on shear bond strength between resin cement and colored zirconia

  • Park, Chan (Department of Prosthodontics, School of Dentistry, Chonnam National University) ;
  • Yoo, Seung-Hwan (Department of Prosthodontics, School of Dentistry, Chonnam National University) ;
  • Park, Sang-Won (Department of Prosthodontics, School of Dentistry, Chonnam National University) ;
  • Yun, Kwi-Dug (Department of Prosthodontics, School of Dentistry, Chonnam National University) ;
  • Ji, Min-Kyung (Department of Prosthodontics, School of Dentistry, Chonnam National University) ;
  • Shin, Jin-Ho (Department of Prosthodontics, School of Dentistry, Chonnam National University) ;
  • Lim, Hyun-Pil (Department of Prosthodontics, School of Dentistry, Chonnam National University)
  • Received : 2016.06.24
  • Accepted : 2016.10.14
  • Published : 2017.04.28
Download PDF
⟨ Previous Next ⟩

Abstract

PURPOSE. To investigate the effect of non-thermal atmospheric pressure plasma (NTAPP) treatment on shear bond strength (SBS) between resin cement and colored zirconia made with metal chlorides. MATERIALS AND METHODS. 60 zirconia specimens were divided into 3 groups using coloring liquid. Each group was divided again into 2 sub-groups using plasma treatment; the experimental group was treated with plasma, and the control group was untreated. The sub-groups were: N (non-colored), C (0.1 wt% aqueous chromium chloride solution), M (0.1 wt% aqueous molybdenum chloride solution), NP (non-colored with plasma), CP (0.1 wt% aqueous chromium chloride solution with plasma), and MP (0.1 wt% aqueous molybdenum chloride solution with plasma). Composite resin cylinders were bonded to zirconia specimens with MDP-based resin cement, and SBS was measured using a universal testing machine. All data was analyzed statistically using a 2-way ANOVA test and a Tukey test. RESULTS. SBS significantly increased when specimens were treated with NTAPP regardless of coloring (P<.001). Colored zirconia containing molybdenum showed the highest value of SBS, regardless of NTAPP. The molybdenum group showed the highest SBS, whereas the chromium group showed the lowest. CONCLUSION. NTAPP may increase the SBS of colored zirconia and resin cement. The NTAPP effect on SBS is not influenced by the presence of zirconia coloring.

Keywords

References

  1. Preis V, Behr M, Kolbeck C, Hahnel S, Handel G, Rosentritt M. Wear performance of substructure ceramics and veneering porcelains. Dent Mater 2011;27:796-804. https://doi.org/10.1016/j.dental.2011.04.001
  2. Aboushelib MN, de Jager N, Kleverlaan CJ, Feilzer AJ. Microtensile bond strength of different components of core veneered all-ceramic restorations. Dent Mater 2005;21:984-91. https://doi.org/10.1016/j.dental.2005.03.013
  3. Heffernan MJ, Aquilino SA, Diaz-Arnold AM, Haselton DR, Stanford CM, Vargas MA. Relative translucency of six all-ceramic systems. Part II: core and veneer materials. J Prosthet Dent 2002;88:10-5.
  4. Yuan JC, Brewer JD, Monaco EA Jr, Davis EL. Defining a natural tooth color space based on a 3-dimensional shade system. J Prosthet Dent 2007;98:110-9. https://doi.org/10.1016/S0022-3913(07)60044-4
  5. Oh GJ, Lee KM, Lee DJ, Lim HP, Yun KD, Ban JS, Lee KK, Fisher JG, Park SW. Effect of metal chloride solutions on coloration and biaxial flexural strength of yttria-stabilized zirconia. Met Mater Int 2012;18:805-12. https://doi.org/10.1007/s12540-012-5009-4
  6. Kim GH, Park SW, Lee K, Oh GJ, Lim HP. Shear bond strength between resin cement and colored zirconia made with metal chlorides. J Prosthet Dent 2015;113:603-8. https://doi.org/10.1016/j.prosdent.2014.12.013
  7. Behr M, Proff P, Kolbeck C, Langrieger S, Kunze J, Handel G, Rosentritt M. The bond strength of the resin-to-zirconia interface using different bonding concepts. J Mech Behav Biomed Mater 2011;4:2-8. https://doi.org/10.1016/j.jmbbm.2010.08.002
  8. Chang JC, Powers JM, Hart D. Bond strength of composite to alloy treated with bonding systems. J Prosthodont 1993;2: 110-4. https://doi.org/10.1111/j.1532-849X.1993.tb00391.x
  9. Blatz MB, Sadan A, Martin J, Lang B. In vitro evaluation of shear bond strengths of resin to densely-sintered high-purity zirconium-oxide ceramic after long-term storage and thermal cycling. J Prosthet Dent 2004;91:356-62. https://doi.org/10.1016/j.prosdent.2004.02.001
  10. Phark JH, Duarte S Jr, Blatz M, Sadan A. An in vitro evaluation of the long-term resin bond to a new densely sintered high-purity zirconium-oxide ceramic surface. J Prosthet Dent 2009;101:29-38. https://doi.org/10.1016/S0022-3913(08)60286-3
  11. von Woedtke T, Metelmann HR, Weltmann KD. Clinical plasma medicine: state and perspectives of in vivo application of cold atmospheric plasma. Contributions Plasma Phys 2014; 54:104-17. https://doi.org/10.1002/ctpp.201310068
  12. Derand T, Molin M, Kvam K. Bond strength of composite luting cement to zirconia ceramic surfaces. Dent Mater 2005; 21:1158-62. https://doi.org/10.1016/j.dental.2005.02.005
  13. Canullo L, Micarelli C, Bettazzoni L, Koci B, Baldissara P. Zirconia-composite bonding after plasma of argon treatment. Int J Prosthodont 2014;27:267-9. https://doi.org/10.11607/ijp.3686
  14. Shim JW, Lee K, Jeong MJ, Jung SC, Kim BH. Hyaluronic acid immobilization on the poly-allylamine coated nano-network $TiO_2$ surface. J Nanosci Nanotechnol 2011;11:7343-6. https://doi.org/10.1166/jnn.2011.4860
  15. Rammelt S, Illert T, Bierbaum S, Scharnweber D, Zwipp H, Schneiders W. Coating of titanium implants with collagen, RGD peptide and chondroitin sulfate. Biomaterials 2006;27: 5561-71. https://doi.org/10.1016/j.biomaterials.2006.06.034
  16. Cales B. Colored zirconia ceramics for dental applications. Bioceram 1998;11:591-4.
  17. Shah K, Holloway JA, Denry IL. Effect of coloring with various metal oxides on the microstructure, color, and flexural strength of 3Y-TZP. J Biomed Mater Res B Appl Biomater 2008;87:329-37.
  18. Ueno T, Kumagai T, Hirota K,Saitoh Y, Kojima I. The characteristic of metal adhesion primer GC Metal Primer II. J Dent Res 1997;76:312.
  19. Beuer F, Erdelt K, Schweiger J, Eichberger M. Flexural strength of coloured and aged zirconia. J Dent Res 2004;83: 942-54.
  20. Bartolome JF, Diaz M, Moya JS. Influence of the metal particle size on the crack growth resistance in mullite-molybdenum composites. J Am Ceram Soc 2002;85:2778-84.
  21. Sbaizero O, Roitti S, Pezzotti G. R-curve behavior of alumina toughened with molybdenum and zirconia particles. Mat Sci Eng A 2003;359:297-302. https://doi.org/10.1016/S0921-5093(03)00366-6
  22. Khan AA, Labbe JC. Aluminium nitride-molybdenum ceramic matrix composites: influence of molybdenum concentration on the mechanical properties. J Mater Sci 1997;32:3829-33. https://doi.org/10.1023/A:1018636025842
  23. Ozcan M, Vallittu PK. Effect of surface conditioning methods on the bond strength of luting cement to ceramics. Dent Mater 2003;19:725-31. https://doi.org/10.1016/S0109-5641(03)00019-8
  24. Kern M, Wegner SM. Bonding to zirconia ceramic: adhesion methods and their durability. Dent Mater 1998;14:64-71. https://doi.org/10.1016/S0109-5641(98)00011-6
  25. Wegner SM, Gerdes W, Kern M. Effect of different artificial aging conditions on ceramic-composite bond strength. Int J Prosthodont 2002;15:267-72.
  26. Luthy H, Loeffel O, Hammerle CH. Effect of thermocycling on bond strength of luting cements to zirconia ceramic. Dent Mater 2006;22:195-200. https://doi.org/10.1016/j.dental.2005.04.016
  27. Silva NR, Coelho PG, Valverde GB, Becker K, Ihrke R, Quade A, Thompson VP. Surface characterization of Ti and Y-TZP following non-thermal plasma exposure. J Biomed Mater Res B Appl Biomater 2011;99:199-206.
  28. Kim JH, Lee MA, Han GJ, Cho BH. Plasma in dentistry: a review of basic concepts and applications in dentistry. Acta Odontol Scand 2014;72:1-12. https://doi.org/10.3109/00016357.2013.795660
  29. Zhang W, Chu PK, Ji J, Zhang Y, Liu X, Fu RK, Ha PC, Yan Q. Plasma surface modification of poly vinyl chloride for improvement of antibacterial properties. Biomaterials 2006;27: 44-51. https://doi.org/10.1016/j.biomaterials.2005.05.067
  30. Yavirach P, Chaijareenont P, Boonyawan D, Pattamapun K, Tunma S, Takahashi H, Arksornnukit M. Effects of plasma treatment on the shear bond strength between fiber-reinforced composite posts and resin composite for core buildup. Dent Mater J 2009;28:686-92. https://doi.org/10.4012/dmj.28.686
  31. Yoshida K, Tsuo Y, Atsuta M. Bonding of dual-cured resin cement to zirconia ceramic using phosphate acid ester monomer and zirconate coupler. J Biomed Mater Res B Appl Biomater 2006;77:28-33.
  32. Valverde GB, Coelho PG, Janal MN, Lorenzoni FC, Carvalho RM, Thompson VP, Weltemann KD, Silva NR. Surface characterisation and bonding of Y-TZP following non-thermal plasma treatment. J Dent 2013;41:51-9. https://doi.org/10.1016/j.jdent.2012.10.002
  33. Amaral R, Ozcan M, Bottino MA, Valandro LF. Microtensile bond strength of a resin cement to glass infiltrated zirconiareinforced ceramic: the effect of surface conditioning. Dent Mater 2006;22:283-90. https://doi.org/10.1016/j.dental.2005.04.021

Cited by

  1. Influence of nonthermal argon plasma on the shear bond strength between zirconia and different adhesives and luting composites after artificial aging vol.10, pp.4, 2018, https://doi.org/10.4047/jap.2018.10.4.308
  2. Polymerization Efficiency of a Dual-Cured Resin Cement through Zirconia with Three Different Cusp Inclinations vol.2018, pp.2314-4939, 2018, https://doi.org/10.1155/2018/8684245
  3. Repair Bond Strength of a Resin Composite to Plasma-Treated or UV-Irradiated CAD/CAM Ceramic Surface vol.8, pp.7, 2018, https://doi.org/10.3390/coatings8070230
  4. Effects of air abrasion and glow-discharge plasma treatment on bonding resin cement to ceria-stabilized zirconia/alumina nanocomposite vol.38, pp.3, 2017, https://doi.org/10.4012/dmj.2018-029
  5. Influence of Non-Thermal Atmospheric Pressure Plasma Treatment on Shear Bond Strength between Y-TZP and Self-Adhesive Resin Cement vol.12, pp.20, 2017, https://doi.org/10.3390/ma12203321
  6. Influence of Low-Pressure Plasma on the Surface Properties of CAD-CAM Leucite-Reinforced Feldspar and Resin Matrix Ceramics vol.10, pp.24, 2017, https://doi.org/10.3390/app10248856
  7. Bonding to zirconia: Effects of translucency and cusp inclinations using an experimental methodology vol.65, pp.3, 2017, https://doi.org/10.2186/jpr.jpr_d_20_00021
  8. Influence of Non-Thermal Atmospheric Pressure Plasma Treatment on Retentive Strength between Zirconia Crown and Titanium Implant Abutment vol.14, pp.9, 2017, https://doi.org/10.3390/ma14092352
  9. Effect of Argon Plasma on the Shear Bond Strength of Y-TZP Zirconia Ceramic Resin Interface vol.10, pp.5, 2017, https://doi.org/10.1149/2162-8777/abfc25
  10. Antibacterial efficacy of non-thermal atmospheric plasma against Streptococcus mutans biofilm grown on the surfaces of restorative resin composites vol.11, pp.1, 2021, https://doi.org/10.1038/s41598-021-03192-0