Abstract
This research investigated the mechanical performance of slurry infiltrated high performance fiber reinforced cementitious composite (SI-HPFRCC) with high volume blast furnace slag powder. Hooked-end steel fibers (volume fraction of 6.4%) were used for the fabrication of SI-HPFRCC. A series of mechanical performance test was conducted including strength and toughness of SI-HPFRCC in compressive and flexural mode at four different ages. Compressive and flexural strength tests of the slurry matrix at the same ages were also conducted in order to evaluate fiber reinforcing effect on the mechanical performance. The flexural response of SI-HPFRCC shows an increasing brittleness with age. The compressive response also shows an increasing brittleness with age but the degree of brittleness is much lower than the flexural case. In terms of strength, SI-HPFRCC shows about 140~190% of compressive strength improvement and 440~500% flexural strength improvement comparing to the slurry matrix.
고비율의 고로슬래그를 사용한 슬러리 충전 고성능 섬유보강 시멘트 복합체(SI-HPFRCC)의 역학적 성능을 평가하였다. SI-HPFRCC 실험체 제작을 위해 hooked-end 형의 강섬유를 6.4% 사용하였다. 재령에 따른 압축강도 및 압축인성과 휨강도 및 휨인성 실험을 통해 SI-HPFRCC의 역학적 성능을 평가하였다. 또한 섬유보강 효과를 평가하기 위해 SI-HPFRCC 실험체 제작에 사용된 슬러리 매트릭스의 압축강도 및 휨강도를 측정하였다. 실험결과 SI-HPFRCC의 휨거동이 재령에 따라 취성이 증가함을 확인하였다. 압축거동의 경우에도 재령에 따른 취성 증가를 볼 수 있었으나 그 정도는 미미하였다. 강도측면에서 볼 때 SI-HPFRCC는 슬러리 매트릭스에 비해 약 140~190%의 압축강도 증가와 440~500%의 휨강도 증가를 보였다.