Effect of Spray-drying Condition and Surfactant Addition on Morphological Characteristics of Spray-dried Nanocellulose

  • Park, Chan-Woo (Department of Forest Biomaterials & Engineering, College of Forest and Environmental Sciences, Kangwon National University) ;
  • Han, Song-Yi (Department of Forest Biomaterials & Engineering, College of Forest and Environmental Sciences, Kangwon National University) ;
  • Namgung, Hyun-Woo (Department of Forest Biomaterials & Engineering, College of Forest and Environmental Sciences, Kangwon National University) ;
  • Seo, Pureun-Narae (Department of Forest Biomaterials & Engineering, College of Forest and Environmental Sciences, Kangwon National University) ;
  • Lee, Seung-Hwan (Department of Forest Biomaterials & Engineering, College of Forest and Environmental Sciences, Kangwon National University)
  • Received : 2017.02.08
  • Accepted : 2017.02.13
  • Published : 2017.02.28

Abstract

In this study, spray-drying yield and morphological characterization of spray-dried cellulose nanofibril (CNF) and TEMPO-oxidized nanocellulose (TONC) depending on spray-drying condition and surfactant addition was investigated. As spray-drying temperature increased, the yield of spray-dried CNF was increased. The highest spray-drying yields in both nanocelluloses were found at didecyl dimethyl ammonium chloride (DDAC) addition of 2.5 phr at all investigated temperatures. The spray-dried CNF was the sphere-like particle, but the spray-dried TONC showed both rod and sphere-like morphology. The average diameter of spray-dried CNF was decreased with increasing DDAC addition amount, resulting in the increase of specific surface area.

Keywords

References

  1. Abe K, Iwamoto S, Yano H. 2007. Obtaining cellulose nanofibers with a uniform width of 15 nm from wood. Biomacromolecules 8: 3276-3278. https://doi.org/10.1021/bm700624p
  2. Henriksson M, Berglund LA, Isaksson P, Lindström T, Nishino T. 2008. Cellulose nanopaper structures of high toughness. Biomacromolecules 9: 1579-1585. https://doi.org/10.1021/bm800038n
  3. Iwamoto S, Abe K, Yano H. 2008. The effect of hemicelluloses on wood pulp nanofibrillation and nanofiber network characteristics. Biomacromolecules 9: 1022-1026. https://doi.org/10.1021/bm701157n
  4. Peng Y, Gardner DJ, Han Y. 2012a. Drying cellulose nanofibrils: in search of a suitable method. Cellulose 19: 91-102. https://doi.org/10.1007/s10570-011-9630-z
  5. Peng Y, Han Y, Gardner DJ. 2012b. Spray-drying cellulose nanofibrils: effect of drying process parameters on particle morphology and size distriution. Wood and Fiber Science 44: 1-14.