Abstract
In this study, acrylic rubber pressure sensitive adhesives was polymerized with 2-ethylhexyl acrylate, styrene, butadiene, 2-hydroxyethyl acrylate, and acrylic acid by controlling the initiator content. The initial tackiness, peel strength, holding power, and heat resistance of the PSAs were investigated by changing the content of tackifier and curing agent. The results showed that the initial tackiness and peel strength increased as the content of tackifier increased, whereas the holding power decreased. Also, the results exhibited that that the initial tackiness, peel strength, and heat resistance decreased as the content of curing agent increased, whereas the holding power and decreased.
본 연구에서는 2-ethylhexyl acrylate, styrene, butadien, 2-hydroxyethyl acrylate, acrylic acid 등의 단량체 조성과 개시제 함량을 조절하여 아크릴고무 점착제를 합성하였다. 제조된 점착제를 이용하여 점착부여제와 경화제를 변화시켜 초기점착력, 점착력, 유지력, 그리고 내열성을 측정함으로써 그 영향을 조사하였다. 실험 결과 개시제의 함량이 증가하면 분자량이 감소하여 초기점착력과 점착력이 증가하였으나, 유지력과 내열성은 감소하는 것을 확인 할 수 있었다. 점착부여제에 따른 물성 변화는 점착부여제의 함량을 높일수록 일정 수준까지는 점착력이 높아 졌으나, 초기점착력과, 유지력, 내열성에서는 함량변화에 따른 물성변화가 크지 않았다. 경화제 함량에 따른 물성 변화는 경화제의 함량을 높일수록 경화밀도가 증가하여, 초기점착력과 점착력은 감소하였고 반면에 유지력과 내열성은 높아지는 경향을 나타내었다.