Abstract
Studies aimed at reducing the occurrence of cracks by the shrinkage of concrete are in demand because the repair and reinforcement for cracks caused by declining concrete durability costs the user to maintain the concrete structure. In particular, in underground power facilities for power transmission, the cost is a heavy burden to repair and reinforce. For this reason, underground power facilities demanded effective methods for crack reduction at the engineering design step. This study, as a part of the development of shrinkage reducing agent for low shrinkage concrete on underground power facilities, investigated TEA to complement the shrinkage reducing agent to improve the early strength of concrete. In the case of TEA 3% as a shrinkage reducing agent, the early strength was improved significantly, and the shrinkage reducing effect was excellent. In addition, TEA 3.0 % and the shrinkage reducing agent 2.0 % showed excellent shrinkage property and compressive strength. On the other hand, more study of shrinkage reducing materials, including performance reviews on the shrinkage reducing materials with variable factors and type of materials, will be needed to generalize these results.
콘크리트의 내구성 저하로 인한 균열의 보수 및 보강에 소요되는 비용은 콘크리트 구조물의 유지비용 증대로 연결되어 균열발생 저감에 대한 연구가 요구되고 있다. 특히, 전력공급용 시설인 전력구의 경우 지하 매설물이므로 보수 및 보강은 경제적으로 큰 부담이 된다. 그러므로 지하매설 전력구의 경우 효과적인 균열 저감 방안이 설계 초기단계부터 요구되어진다. 본 연구는 전력구용 저수축 콘크리트 제조를 위한 수축저감제 개발의 일환으로 수축저감제 사용 콘크리트의 초기 강도 개선을 위해 TEA를 검토하였다. 검토결과, TEA를 수축저감제의 3% 사용할 경우 조기 강도가 크게 개선되었으며, 수축저감 효과도 우수한 것으로 확인되었다. 또한, TEA 3 %에 수축저감제 2.0 % 혼합하여 적용하였을 경우 압축강도 특성 및 건조수축 길이변화 실험결과에서 가장 우수한 것으로 나타나 수축저감제로서의 가능성을 확인하였다. 추후 수축저감제의 범용적인 적용성 검토를 위하여 수축저감제의 사용재료 변화 등에 대한 다양한 재료변수 요인 검토를 통하여 수축저감제의 성능 검토가 필요할 것으로 사료된다.