Abstract
In order to evaluate corrosion resistance of steel fiber-reinforced concrete, accelerated chloride migration and surface resistivity tests were conducted. In addition air content of fresh concrete, compressive strength and water absorption were measured for investigating fundamental characteristics of concrete. Two different water-cement ratios(0.44, 0.5) and three steel fiber contents(0.25%, 0.5%, 1%) were considered as variables. Note that all specimens cast with same compaction work. As a results, corrosion resistance decreased as steel fiber contents increased regardless of water-cement ratio when the concrete was compacted with same amount of work done. However, for concrete with same steel fiber content, the lower water-cement ratio showed the better corrosion resistance. It is found that enhancement of fluidity and enough compaction should be done for corrosion resistance of SFRC.
본 연구에서는 강섬유보강콘크리트의 부식저항성능을 규명하기 위한 촉진염소이온확산시험과 표면전기저항시험을 수행하였다. 또한 배합평가를 위한 기초시험으로서 굳지 않은 콘크리트 공기량, 일축압축강도, 굳은 콘크리트의 흡습시험을 수행하였다. 실험변수는 두 종류의 물-시멘트비(0.44, 0.50)와 세 개의 강섬유 혼입량(0.25%, 0.5%, 1%)으로 선정하였다. 주목할 것은 모든 타설시 콘크리트의 다짐량은 동일하게 하였다. 시험결과, 동일한 작업량으로 다짐이 되었을 때, 물-시멘트비에 상관없이 두배합 모두에서 강섬유 혼입률이 증가함에 따라 부식저항성능이 감소하는 것으로 확인되었다. 그러나, 동일한 강섬유 혼입비에 대하여 배합의 물-시멘트비가 낮은 콘크리트의 부식저항성능이 우수한 것으로 나타났다. 따라서, 강섬유보강콘크리트의 타설시 유동성의 확보와 충분한 다짐이 염소이온침투저항성능을 확보하기 위하여 매우 중요하다고 판단된다.