Emission Characteristics of Multi-Tandem OLED using MoOx with CGL

CGL 층으로 MoOx를 사용한 다중 적층구조 OLED의 발광 특성

  • Kim, Ji-Hyun (Department of Advanced Materials Science and Engineering, Daejin University) ;
  • Ju, Sung-Hoo (Department of Advanced Materials Science and Engineering, Daejin University)
  • 김지현 (대진대학교 신소재공학과) ;
  • 주성후 (대진대학교 신소재공학과)
  • Received : 2015.06.16
  • Accepted : 2015.06.29
  • Published : 2015.06.30

Abstract

We studied emission characteristics of blue fluorescent multi-tandem OLEDs using $Al/MoO_x$ as charge generation layer(CGL). Threshold voltage for 2, 3, 4, and 5 units tandem OLEDs was 8, 11, 14 and 18 V, respectively. The threshold voltage in multi-tandem OLEDs was lower than multiple of 4 V for the single OLED. Maximum current efficiency and maximum quantum efficiency of single OLED were 7.6 cd/A and 5.5%. Maximum current efficiency for 2, 3, 4, and 5 units tandem OLEDs was 22.6, 31.4, 41.2, and 46.6 cd/A, respectively. Maximum quantum efficiency for 2, 3, 4, and 5 units tandem OLEDs was 11.8, 15.8, 21.8, and 25.6%, respectively. The maximum current efficiency and maximum quantum efficiency in multi-tandem OLEDs were higher than multiple of those for the single OLED. The intensity for 508 nm peak was changed and the peak wavelength was red shift by increase of tandem unit in electroluminescent emission spectra. These phenomena can be caused by micro-cavity effect with increasing of organic layer thickness.

Keywords

References

  1. C.W. Tang, S.A. Vanslyke, Appl. Phys. Lett., 51 (1987) 913. https://doi.org/10.1063/1.98799
  2. J. Clark, G. Lanzani, Nature, 4 (2010) 438.
  3. T. Tsutsui, M. Terai, Appl. Phys. Lett., 84 (2004) 440. https://doi.org/10.1063/1.1640470
  4. T. Tsutsui, M. Terai, Appl. Phys. Lett., 90 (2007) 083502. https://doi.org/10.1063/1.2709519
  5. Fawen Guo, Dongge Ma, Appl. Phys. Lett., 87 (2005) 173510. https://doi.org/10.1063/1.2120898
  6. Ping Chen, Wenfa Xie, Jiang Li, Tao Guan, Yu Duan, Yi Zhao, Shiyong Liu, Chunsheng Ma, Liying Zhang, Bin Li, Appl. Phys. Lett., 91 (2007) 023505. https://doi.org/10.1063/1.2757096
  7. P. S. Vincentt, W. A. Barlow, R. A. Hann, G. G.Roberts, Thin Solid Film, 94 (1982) 171. https://doi.org/10.1016/0040-6090(82)90509-0
  8. R. H. Partridge, Polymer, 24 (1983) 748. https://doi.org/10.1016/0032-3861(83)90014-9
  9. C. W. Tang, S. A. VanSlyke, Appl. Phys. Lett., 51 (1987) 913. https://doi.org/10.1063/1.98799
  10. T. Chiba, Y. J. Pu, R. Miyazaki, K. Nakayama, H. Sasabe, J. Kido, Organic Electronics, 12 (2011) 710. https://doi.org/10.1016/j.orgel.2011.01.022
  11. T. H. Kwak, S. H. Ju, J. Kor. Inst. Surf. Eng., 47 (2014) 104. https://doi.org/10.5695/JKISE.2014.47.3.104
  12. M. Liu, P. Chen, Q. Xue, F. Jianga, G. Xie, J. Hou, Y. Zhao, L. Zhang, B. Li, Microelectronics Journal, 39 (2008) 1622. https://doi.org/10.1016/j.mejo.2008.02.018
  13. C. H. Chang, Z. J. Wu, Y. H. Liang, Y. S. Chang, C. H. Chiu, C. W. Tai, H. H. Chang, Thin Solid Films, 548 (2013) 389. https://doi.org/10.1016/j.tsf.2013.08.084
  14. T. Chib, Y. Pu, R. Miyazaki, K. Nakayam, H. Sasabe, J. Kido, Organic Electronics, 12 (2011) 710. https://doi.org/10.1016/j.orgel.2011.01.022
  15. Peng, H., Sun, J., Zhu, X., Yu, X., Wong, M., and Kwok, H.-S., Appl. Phys. Lett., 88 (2006) 073517. https://doi.org/10.1063/1.2172734
  16. Wu, C. C., Hsieh, P. Y., Lin, C. L., and Chiang, H. H., Appl. Phys. Lett., 84 (2004) 3966. https://doi.org/10.1063/1.1745107
  17. Chang, C.-H., Cheng, H.-C., Lu, Y.-J., Tien, K.-C., Lin, H.-W., Lin, C.-L., Yang, C.-J., and Wu, C.- C., Org. Electron., 11 (2010) 247. https://doi.org/10.1016/j.orgel.2009.11.002

Cited by

  1. Emission Characteristics of White Tandem Organic Light Emitting Diodes Using Blue and Red Phosphorescent Materials vol.49, pp.2, 2016, https://doi.org/10.5695/JKISE.2016.49.2.196