Abstract
In order to achieve high flexibility in manufacture, analysis of chip's shape is one of the most important problems. This paper describes the change of machining characteristics in workpiece materials depending on turning clearance angle. The experiments start from choosing three workpiece materials that are SM45C(machine structural carbon steel), STS303(stainless steel), SCM415 (chrome-molybdenum steel). Then, the experiments show specifically how features of selected materials changed when they were processed with diverse machining depths and with feed rate starting from fixed rotational speed. Especially, the experiments were also analyzed in chip's shape and wear of insert tip. In conclusion, these experiments show that chip's shape was changed by quality of the materials, depth of cut, and conveying speed. When machining feedrate and machining depth were 0.10mm/rev and 0.3mm respectively, workpiece materials showed the best shapes, not categorizing quality of the materials and machining characteristics.
상품을 제조할 때 유연성을 높이기 위해서는 칩의 형상분석이 중요한 문제 중의 하나이다. 본 연구에서는 선삭 작업에서 가공 여유각 변경에 따른 피삭재의 가공특성이 어떻게 변화되는지 분석하고 자 하였다. 피삭재는 3가지로 SM45C(기계구조용탄소강), SCM415(크롬몰리브덴강), STS303(스테인리스강)을 선택하여 정해진 가공조건인 회전속도, 이송속도와 가공 깊이에 따라 분석하였다. 특히, 선삭가공에서의 칩의 형상과 인서트 팁의 마모현상을 분석하였다. 결과적으로 칩의 형상은 피삭재의 재질과 가공깊이, 이송속도에 따라 변화됨을 알 수 있었다. 가공이송속도가 0.10mm/rev일 때와 가공깊이 0.3mm일 때가 유동형 칩으로 재질이나 가공특색을 분류하지 않고 가장 좋은 형상을 보였다.