A study on different failure criteria to predict damage in glass/polyester composite beams under low velocity impact

  • Aghaei, Manizheh (Department of mechanical engineering, Isfahan University of Technology) ;
  • Forouzan, Mohammad R. (Department of mechanical engineering, Isfahan University of Technology) ;
  • Nikforouz, Mehdi (Department of mechanical engineering, Isfahan University of Technology) ;
  • Shahabi, Elham (Department of mechanical engineering, Isfahan University of Technology)
  • 투고 : 2014.05.21
  • 심사 : 2014.11.23
  • 발행 : 2015.05.25

초록

Damage caused by low velocity impact is so dangerous in composites because although in most cases it is not visible to the eye, it can greatly reduce the strength of the composite material. In this paper, damage development in U-section glass/polyester pultruded beams subjected to low velocity impact was considered. Different failure criteria such as Maximum stress, Maximum strain, Hou, Hashin and the combination of Maximum strain criteria for fiber failure and Hou criteria for matrix failure were programmed and implemented in ABAQUS software via a user subroutine VUMAT. A suitable degradation model was also considered for reducing material constants due to damage. Experimental tests, which performed to validate numerical results, showed that Hashin and Hou failure criteria have better accuracy in predicting force-time history than the other three criteria. However, maximum stress and Hashin failure criteria had the best prediction for damage area, in comparison with the other three criteria. Finally in order to compare numerical model with the experimental results in terms of extent of damage, bending test was performed after impact and the behavior of the beam was considered.

키워드

참고문헌

  1. Batra, R.C., Gopinath, G. and Zheng, J.Q. (2012), "Damage and failure in low energy impact of fiber-reinforced polymeric composite laminates", Compos. Struct., 94(2), 540-547. https://doi.org/10.1016/j.compstruct.2011.08.015
  2. Chang, F. and Chang, K. (1987), "A progressive damage model for laminated composites containing stress concentrations", Compos. Mater., 21(9), 834-855. https://doi.org/10.1177/002199838702100904
  3. Cui, H., Wen, W. and Cui, H.T. (2009), "An integrated method for predicting damage and residual tensile strength of composite laminates under low velocity impact", Comput. Struct., 87(7-8), 456-466. https://doi.org/10.1016/j.compstruc.2009.01.006
  4. Donadon, M.V., Iannucci, L., Falzon, B.G., Hodgkinson, J.M. and Almeida, S.F.M. (2008), "A progressive failure model for composite laminates subjected to low velocity impact damage", Comput. Struct.,86(11-12), 1232-1252. https://doi.org/10.1016/j.compstruc.2007.11.004
  5. Donadon, M.V., Almeida, M., Arbelo, M.A. and Faria, A. (2009), "A three-dimensional ply failure model for composite structures", Int. J. Aerosp. Eng., 9, 1-22.
  6. Garnich, M. and Akula, V. (2008), "Review of degradation models for progressive failure analysis of fiber reinforced polymer composites", Appl. Mech. Rev., 62(1), 010801. https://doi.org/10.1115/1.3013822
  7. Icardi, U., Locatto, S. and Longo, A. (2007), "Assessment of recent theories for predicting failure of composite laminates", Appl. Mech. Rev. ASME, 60(2), 76-86. https://doi.org/10.1115/1.2515639
  8. Irhirane, E.H., Abousaleh, M., Echaabi, J., Hattabi M., Saouab, A. and Bensalah, M.O. (2010), "Modeling and simulation of the failure and stiffness degradation of a graphite epoxy in a three Point bending test", J. Eng. Mater. Tech. ASME, 132(3), 1-8.
  9. Johnson, H.E., Louca, L.A. and Mouring, S.E. (2006), "Damage modeling of large and small scale composite panels subjected to a low velocity impact", HSE Report.
  10. Khalili, S.M.R., Soroush, M., Davar, A. and Rahmani, O. (2011), "Finite element modeling of low-velocity impact on laminated composite plates and cylindrical shells", Compos. Struct., 93(5), 1363-1375. https://doi.org/10.1016/j.compstruct.2010.10.003
  11. Menna, C., Asprone, D., Caprino, G., Lopresto, V. and Prota, A. (2011), "Numerical simulation of impact tests on GFRP composite laminates", Int. J. Impact Eng., 38(8-9), 677-685. https://doi.org/10.1016/j.ijimpeng.2011.03.003
  12. Minak, G., Ghelli, D., Panciroli, R. and Zucchelli, A. (2009), "Composite tube behavior under low velocity impact", Mech. Solid. Brazil, pp. 385-398.
  13. Sanchez-Saez, S., Barbero, E. and Navarro, C. (2007), "Analysis of the dynamic flexural behavior of composite beams at low temperature", Compos. Sci. Technol.. 67(11-12), 2616-2132. https://doi.org/10.1016/j.compscitech.2006.12.002
  14. Santiuste, C., Sanchez-Saez, S. and Barbero, E. (2010), "A comparison of progressive-failure criteria in the prediction of the dynamic bending failure of composite laminated beams", Compos. Struct., 92(10), 2406-2414. https://doi.org/10.1016/j.compstruct.2010.03.004
  15. Sutherland, L.S. and Guedes Soares, C. (2005), "Impact on low fibre-volume, glass/polyester rectangular plates", Compos. Struct., 68(1), 13-22. https://doi.org/10.1016/j.compstruct.2004.02.010
  16. Tan, S.C. and Perez, J. (1993), "Progressive failure of laminated composites with a hole under compressive loading", Reinf. Plast. Compos., 12(10), 1043-1057. https://doi.org/10.1177/073168449301201002
  17. Tiberkak, R., Bachene, M., Rechak, S. and Necib, B. (2008), "Damage prediction in composite plates subjected to low velocity impact", Compos. Struct., 83(1), 73-82. https://doi.org/10.1016/j.compstruct.2007.03.007

피인용 문헌

  1. A damage mechanics based failure criterion for fiber reinforced polymers vol.140, 2017, https://doi.org/10.1016/j.compscitech.2016.12.023
  2. Polypropylene fiber reinforced concrete plates under fluid impact. Part I: experiments vol.60, pp.2, 2016, https://doi.org/10.12989/sem.2016.60.2.211
  3. Investigation of natural solution effect in electrical conductivity of PANI-CeO2 nanocomposites vol.24, pp.1, 2015, https://doi.org/10.12989/scs.2017.24.1.015
  4. Ultimate strength estimation of composite plates under combined in-plane and lateral pressure loads using two different numerical methods vol.29, pp.6, 2018, https://doi.org/10.12989/scs.2018.29.6.785
  5. Combined effects of end-shortening strain, lateral pressure load and initial imperfection on ultimate strength of laminates: nonlinear plate theory vol.33, pp.2, 2015, https://doi.org/10.12989/scs.2019.33.2.245
  6. A new replaceable fuse for moment resisting frames: Replaceable bolted reduced beam section connections vol.35, pp.3, 2015, https://doi.org/10.12989/scs.2020.35.3.353