Abstract
In this study, a variety of industrial gears, shafts, chains, rollers, mold, etc. are widely used inautomotive steel carbon steel for machine structural SM45C typical material used for the experiments. In order to cure the surface of the test piece after the rough grinding and fine grinding was performed in order polishing. Perform the surface hardening of SM45C lacal area by using a diode laser. The output of the laser diode and the feed rate to the process variable. Micro-hardness testing, microstructure testing, scanning electron microscope testing(SEM), the heat input to the analysis. After analyzing the experiment to compare the mechanical properties of the material. When using a diode laser to assess the soundness of the surface hardening. Accordingly, the process for deriving the optimum demonstrate the feasibility.
본 연구에서는 산업현장에서 각종 기어나, 축, 체인, 롤러, 금형, 자동차강판 등으로 널리 쓰여 지는 기계구조용 탄소강인 SM45C를 실험소재로 사용하였다. 실험에 사용되는 시험편 표면에 표면경화를 수행하기 위하여 #200 ~ #1500의 순서대로 미세연마 후 거친연마의 연마가공을 실시하였으며, 다이오드 레이저의 표면경화 열처리 후에 자기냉각효과를 고려하여 $100{\times}50{\times}10$의 판재로 시험편을 제작하여 실험하였다. 소재 표면에 다이오드 레이저를 이용하여 국소부위에 표면경화 열처리를 수행하였다. 이때 다이오드 레이저의 출력과 이송속도를 공정조건으로 하여, 미세경도시험, 미세조직시험, 전자 주사 현미경(SEM), 입열량을 분석하였다. 분석 후에는 실험소재의 기계적 특성을 비교하여, 타 표면 경화법에 비해 다이오드 레이저를 이용하였을 때의 표면경화 열처리 신뢰성과 우수함 그리고 최적의 공정조건을 도출하였다. 열처리 후 경화부는 판상 마르텐사이트로 경화 되었으며. 경도값은 Hv729.5로 열처리 후 약 2.3배 이상 표면경도가 향상되있는 것을 확인하였다.