Abstract
This paper presents the results of experimental investigations on the shear failure behaviors of reinforced concrete beams using ductile fiber reinforced cementitious composite (DFRCC). Total 10 RC beams of $150{\times}300{\times}1,000mm$ size were tested by 4-point bending under the displacement control. The main parameters of the experiment are surface treatment by grinding and preloading to the cracking point in the repair process. The load-displacement curves, diagonal tension cracking load, flexural cracking load, and shear strength were obtained. The test results showed that the DFRCC can be used effectively for restoring the shear strength approximately 99% to the original value under the condition that the appropriate thickness and surface treatment like grinding are assured. For further research, the specimens taken from real deteriorated structures will need to be tested after being repaired with DFRCC.
본 논문에서는 고인성 섬유 시멘트 복합재료(DFRCC)를 이용한 철근콘크리트(RC) 보의 전단파괴거동에 대한 실험적 연구결과를 제시하였다. 이를 위해 $150{\times}300{\times}1,000mm$ 크기의 보를 총 10개 제작하여 변위제어에 의한 4점휨파괴실험을 실시하였다. 주요 실험변수로는 DFRCC에 의한 보강의 유무, 보강시 그라인딩을 통한 사전 표면처리 그리고 사전 균열발생 유무를 설정하였다. 실험으로부터 재하시작 후 파괴시까지 보의 하중-처짐곡선, 전단균열 및 휨균열 발생하중 그리고 파괴시 전단강도를 측정하였다. 실험결과, DFRCC에 의한 보강시 적절한 두께와 사전 표면처리를 적절히 시행할 경우 기존 RC보의 전단강도를 약 99% 이상 효과적으로 복원할 수 있는 것으로 나타났으며, 보다 신뢰성있는 연구를 위하여 실제 노후화된 구조물에서 채취한 부재에 대한 추가적인 실험과 이론적 연구가 필요한 것으로 판단된다.