Abstract
Currently, demand of liquefied natural gas as an alternatice energy inceases because of depletion of fossil fuels. it is accompanied by inceasing demand of LNG ship. Consequentially, it is expected that demand of bellows for LNG ship increase. The material used for LNG vessels's bellows is an alloy of INCOLOY 825 and STS316L, which are strong against low-temperature brittleness and seawater corrosion. This study establishes the welding condition of LNG vessel's bellows material in extremely low temperature, and analyzes the formability of weld through Erichsen Test. When welding was conducted at optimal condition, tensile strength of weld presneted strength value up to 90% compared with base metal. As results of formalbility through Erichsen test, very good weld that failure occrued in base metal was gotten.
최근 기존 화석연료의 고갈로 인하여 대체에너지로써 천연액화가스의 수요 증가와 함께 LNG 운반선의 수요가 증가하고 있으며, 그로인해 극한의 환경에서 사용할 수 있는 LNG 선박용 벨로우즈의 수요 또한 증가할 것으로 예상된다. 현재 LNG 선박용 벨로우즈에 사용되는 재료는 저온취성과 해수부식에 강한 INCOLOY 825와 STS316L합금이다. 본 연구에서는 극저온에 사용되는 LNG용 벨로우즈 재질인 INCOLOY 825과 STS316L 합금에 대하여 최적의 용접조건을 설정하고, 에릭센 시험을 통하여 용접부의 성형성을 분석하였다. 최적 조건에서의 용접시 용접부의 인장강도는 모재에 비하여 90% 이상의 강도값을 나타내었다. 또한 에릭센 시험을 통한 성형성 분석의 결과, 용접부가 아닌 모재에서 파단이 발생하는 매우 양호한 용접부를 얻을 수 있었다.