The Effects of (Ba0.4Ca0.6)SiO3 Nano Spheroidization Glass Additives on the Microstructure and Microwave Dielectric Properties of Ba(Zn1/3Ta2/3)O3 Ceramics

  • Received : 2014.01.10
  • Accepted : 2014.05.06
  • Published : 2014.09.01

Abstract

In this study, the microwave dielectric properties of nano spheroidization glass powders added $Ba(Zn_{1/3}Ta_{2/3})O_3$ ceramics prepared by solid state reaction have been investigated. Adding $(Ba_{0.4}Ca_{0.6})SiO_3$ nano spheroidization glass powders could effectively promote the densification even in the case of decreasing the sintering temperature. When the glass frit is 0.3 wt% and sintering is carried out at a temperature of $1500^{\circ}C$ for 6 hr, a temperature stable microwave dielectric ceramic could be obtained, which has a dielectric constant (${\varepsilon}_r$) of 30.2, a quality factor ($Q{\times}f_0$) of 124,000 GHz and a temperature coefficient of resonance frequency (${\tau}_f$) of $2ppm/^{\circ}C$.

Keywords

1. Introduction

With the recent development of the wireless communication field, there has been a development from communication service mainly for voice transmission and reception to various multimedia application services. According to the requirements for various multimedia application services, an increase in the frequency of use and the use of a high-frequency of 60GHz, 77GHz or 94GHz that enables broadband services have been reviewed. Thus, the requirement for a microwave dielectric resonator having high performance, which can be used in this high-frequency band, has increased. The three important characteristics required for a microwave dielectric resonator are suitable dielectric constant for use, a high quality factor (Q×fo), and a stability of the temperature coefficient of resonant frequency [1]. Typical compositions having a high quality factor among microwave dielectric properties include complex perovskite A2+(B2+1/3B5+2/3)O3, wherein the A-site includes Ba or Sr, and the B-site includes divalent ions such as Zn or Mg, or pentavalent ions such as Ta or Nb. Among them, typical compositions include Ba(Zn1/3Ta2/3)O3 known to have a quality factor (Q×fo), higher than 120,000 and a stable temperature coefficient of resonant frequency [2,3]. It is known that, to increase the quality factor of this composition, the ordering of the B-site (Zn and Ta) is required, and for this ordering, heat treatment at a temperature of 1600 ℃ or higher for a long time is required [4,5,6]. Methods that are generally used to lower the sintering temperature of microwave dielectric ceramics include a method of reducing the size of power, a method of adding V2O5, CuO, SiO2, B2O3 and the like as sintering aids for promoting liquid-phase sintering, or a method of adding glass powder that forms a liquid phase by itself [7]. Addition of glass powder for lowtemperature sintering is effective in lowering the sintering temperature, but results in deterioration in microwave dielectric properties due to a glass phase remaining after sintering. Glass powder compositions that are generally added to microwave dielectric materials include lanthanum borate glass (20RO-20La2O3-60B2O3; R = Ca, Mg, Zn), anorthite glass (CaO-Al2O3-2SiO2) and the like. A mutilayer ceramic capacitor (MLCC) that is a typical part composed of a dielectric material is manufactured using barium calcium silicate glass (BaO-CaO-SiO2) or borosilicate glass (R2O-B2O3-SiO2; R: alkali metal) in order to lowtemperature and dielectric characteristics [8, 9]. In this study, various amounts of barium calcium silicate-based nano spheroidization glass powders synthesized by a radiofrequency (RF) thermal plasma process were added to Ba(Zn1/3Ta2/3)O3, and the crystalline phases and microstructures of the microwave dielectric ceramics were analyzed. In addition, the dielectric properties of the microwave dielectric materials were studied.

 

2. Experimental Method

As starting materials for preparing a Ba(Zn1/3Ta2/3)O3 composition, BaCO3 (99.9%, Sakai, Japan), ZnO (99.9%, Kojundo Chemical, Japan) and Ta2O5 (99.9%, Kojundo Chemical, Japan) were used. Ba(Zn1/3Ta2/3)O3 was mixed using a general ceramic process, and the powder was calcined at a temperature of 1200 ℃ for 2 hours. Nano spheroidization glass powder was added to the calcined powder, and the mixture was mixed and ground using ethanol and zirconia balls. The powder was added to PVA, after which it was granulated, and then molded using a disk mold, and the molded sample was sintered at 1400 ~ 1550 ℃ for 4 hr. As raw materials for the RF thermal plasma treatment, nano spheroidization glass powder with the composition of SiO2-0.4BaO-0.6CaO was prepared by the following procedure. Reagent-grade SiO2, BaCO3, and CaCO3 (Kojundo chemical, Japan) were weighed in the composition ratio and ball-milled in ethanol with zirconia balls for 24 hr. The dried powders were melted at 1550 ℃ for 1 h using a platinum crucible, and the melted mixture was poured into a twin roller to produce a glass cullet. These cullet flakes were ball milled into glass powders with an average size of ~1㎛. The sub-micrometer-sized coarse glass powders were nano spheroidized using the RF thermal plasma system (model TDU-60, Tekna Plasma System Inc., Canada). The induction plasma powder synthesis was performed at pressure of 80~100 torr and 30~50 kW of power under a flow rate of 20 slpm (standard liter per minute) of Ar as a central gas and 80 slpm of O2 as a sheath gas. The crystallization temperature of glass was analyzed using thermogravimetry (TG-DTA SDT Q-600, TA Instruments) at a heating rate of 20 ℃/min. The phases of the sintered sample were analyzed by X-ray diffraction (XRD) using Cu-Kα rays in the range of 20-60°. The surface of the sintered sample was polished and thermally etched, and then the microstructures were observed using a scanning electron microscope (SEM). The dielectric constant (ε) was measured using the Hakki-Coleman method, and the quality factor (Q×f0) was measured using the cavity perturbation method that shows high accuracy [10, 11]. The temperature coefficient of resonant frequency (τf) was determined by placing the sample in a cavity resonator made of copper and measuring the resonant frequencies f25 and f 80 at room temperature and 80 ℃.

 

3. Results and Discussions

Fig. 1 shows the shape and the results of DTA analysis of nano spheroidization glass powder. As shown in Fig. 1, plasma-treated glass powders have a spherical shape, an average particle size (D50) of 120 nm and a BET surface area of 13.86 m2/g. The results of thermo gravimetric analysis (TGA) indicate that the of nano spheroidization glass powder have a Tg of 651℃, a crystallization initiation temperature of 799℃ and a main crystallization temperature of 926℃.

Fig. 1.The DTA results and powder shape with plasma treated nano spheroidization glass powder: (a) Powder shape with plasma treated glass powder; (b) The DTA results with plasma treated nano spheroidization glass powder.

Fig. 2 shows the results of XRD analysis of Ba(Zn1/3Ta2/3)O3 ceramics as a function of nano spheroidization glass powder content and sintered at 1450℃. As can be seen in Fig. 2, the main peak is shifted to a higher angle due to the addition of nano spheroidization glass powder, and a secondary phase is produced as the of nano spheroidization glass powder content increases.

Fig. 2.XRD results of sintered BZT ceramics with nano spheroidization glass powder addition: (a) glass powder (0.0 wt%); (b) glass powder (0.3 wt%); (c) glass powder (0.6 wt%) (d) glass powder (1.0 wt%)

Fig. 3 shows the changes in bulk density of Ba(Zn1/3Ta2/3)O3 ceramics as a function of nano spheroidization glass powder content and sintering temperature. As can be seen therein, at a sintering temperature of 1500℃, the density increases as the nano spheroidization glass powder content and the sintering temperature increase, but at a nano spheroidization glass powder content of 1.0 wt%, the bulk density significantly decreases regardless of the sintering temperature. Generally, in the case of pure Ba(Zn1/3Ta2/3)O3, a sintering temperature of 1600℃ or a long sintering time is required to obtain a bulk density of 7.953 g/cm3 or higher, but a bulk density of 7.53 g/cm3 is shown even at a nano spheroidization glass powder content of 0.3 wt%, suggesting that the sintering temperature can be lowered by the addition of nano spheroidization glass powder.

Fig. 3.Bulk density of BZT ceramics according to sintering temperature for various nano spheroidization glass powder addition

Fig. 4 shows the microstructures of the sintered sample having nano spheroidization glass powder contents and sintered at a temperature of 1500℃. As can be seen therein, the microstructures become more dense and angular as the glass powder content increases. In the case of nano spheroidization glass powder content 1.0 wt%, the microstructures look dense, but the bulk density decreases, and this decrease in the bulk density is believed to be because of abnormal grain growth caused by excessive liquid-phase sintering and the influence of a secondary phase caused by glass. Fig. 5 shows the changes in dielectric constant of Ba(Zn1/3Ta2/3)O3 ceramics as a function of nano spheroidization glass powder content and sintering temperature. As can be seen therein, in the case of pure Ba(Zn1/3Ta2/3)O3, the dielectric constant increases as the sintering temperature increases, and a dielectric constant of 30 or higher is shown at a sintering temperature of 1550℃ or higher. In the cases of Ba(Zn1/3Ta2/3)O3 ceramics containing nano spheroidization glass powder, a dielectric constant of 30 or higher is shown even at a sintering temperature of 1450℃. It is generally known that, when glass powder having a low dielectric constant is added to a dielectric material, the dielectric constant of the dielectric material is reduced [7]. However, the Ba(Zn1/3Ta2/3)O3 ceramics having a nano spheroidization glass powder content of 0.3 wt% or lower showed a dielectric constant similar to that of pure Ba(Zn1/3Ta2/3)O3, suggesting that nano spheroidization glass powder was solid-dissolved in Ba(Zn1/3Ta2/3)O3 without forming a secondary phase. It is known that the increase in dielectric constant of a dielectric material with an increase in sintering temperature is determined by the composition of the dielectric material, but in the case of the same composition, the dielectric constant increases as the grain size increases. However, it is believed that the increase in dielectric constant with an increase in sintering temperature in this experiment is due to bulk density.

Fig. 4.SEM image of sintered BZT ceramics with nano spheroidization glass powder addition: (a) glass powder (0.0 wt%); (b) glass powder (0.3 wt%); (c) glass powder (0.6 wt%); (d) glass powder (1.0 wt%)

Fig. 5.Dielectric constant of BZT ceramics according to sintering temperature for various nano spheroidization glass powder addition

Fig. 6 shows the changes in quality factor (Q×fo) of Ba(Zn1/3Ta2/3)O3 ceramics as a function of nano spheroidization glass powder content and sintering temperature. As can be seen therein, in the case of pure Ba(Zn1/3Ta2/3)O3, the quality factor (Q×fo) value increases as the sintering temperature increases, and in the case of Ba(Zn1/3Ta2/3)O3 ceramics containing glass powder, at a sintering temperature of 1500℃ or lower, the quality factor (Q×fo) value increases as the nano spheroidization glass powder content increases, but at a sintering temperature of 1550℃, the quality factor value decreases as the nano spheroidization glass powder content increases. It is generally known that the quality factor of a dielectric material is greatly influenced by the composition and microstructure of the dielectric material, and a combination of point defects, grain boundaries, voids, secondary phases and the like is attributable to a decrease in quality factor. In particular, it is known that the quality factor (Q×fo) of complex perovskite A(B', B")O3 is influenced by the ordering of Zn and Ta ions at the B lattice position. It is believed that the increase in the quality factor (Q×fo) value with an increase in sintering temperature is attributable to the ordering of ions as previously reported and that the decrease in quality factor by the addition of nano spheroidization glass powder is attributable to a secondary phase caused by the glass phase. The temperature coefficient of resonant frequency that is the important property of a dielectric resonator was in the range of 3-7.5 ppm/℃ for pure Ba(Zn1/3Ta2/3)O3 depending on the sintering temperature and time, and this temperature coefficient value was shown to be similar to a previously reported value [2, 3, 4]. In the case of Ba(Zn1/3Ta2/3)O3 ceramics containing glass powder, the temperature coefficient of resonant frequency decreased as an increase in the nano spheroidization glass powder content and was shown to range from -7 to 2 ppm/℃. The temperature coefficient of resonant frequency is influenced by the temperature coefficient of dielectric constant (τε) and the coefficient of thermal expansion (αl). It can be seen that the decrease in the temperature coefficient of resonant frequency with an increase in the nano spheroidization glass powder content is attributable to the change in thermal expansion coefficient by the glass phase.

Fig. 6.Quality factor of BZT ceramics according to sintering temperature for various nano spheroidization glass powder addition

 

4. Conclusion

In this study, nano spheroidization glass powder was added to a composition of Ba(Zn1/3Ta2/3)O3, and the microwave dielectric properties and microstructures of the resulting Ba(Zn1/3Ta2/3)O3 ceramics having glass powder contents and sintered at various temperatures were examined. The experimental results revealed that, as the nano spheroidization glass powder content increased, the microstructures of the dielectric ceramics became denser even at low temperatures. On the other hand, in the case of the microwave dielectric properties of the dielectric ceramics, it could be seen that the dielectric constant and the quality factor decreased as the nano spheroidization glass powder content increased. Excellent microwave dielectric properties could be obtained under the conditions of suitable nano spheroidization glass powder content and sintering temperature. Particularly, when the nano spheroidization glass powder is 0.3 wt% and sintering is carried out at a temperature of 1500℃ for 6 hr, a temperature stable microwave dielectric material is obtained, which has a dielectric constant (εr) of 30.2, a quality factor (Q×fo) of 124,000 GHz and a temperature coefficient of resonance frequency (τf) of 2 ppm/℃.

References

  1. Ian M. Reaney, David Iddles, "Microwave dielectric ceramics for resonators and filters in mobile phone networks" J. Am. Ceram. Soc. 89(7), pp. 2063-2072, 2006.
  2. Syunichiro Kawashima, Masamitsu Nishida, Ichiro Ueda, Hiromu Ouchi, "$Ba(Zn_{1/3}Ta_{2/3})O_{3}$ Ceramics with Low Dielectric Loss at Microwave Frequencies," J. Am. Ceram. Soc. pp. 421-423, 1983.
  3. L.Nedelcu, M.I.Toacsan, M.G.Banciu, A.Ioachim, "Microwave properties of $Ba(Zn_{1/3}Ta_{2/3})O_{3}$ dielectric resonators." Journal of Alloys and Compounds 509 (2), pp. 477-481, 2011. https://doi.org/10.1016/j.jallcom.2010.09.069
  4. Mario Bieringer, Sandra M. Moussa, Liam D. Noailles, Andrew Burrows, Christopher J. Kiely, Matthew J. Rosseinsky, and Richard M. Ibberson, "Cation Ordering, Domain Growth, and Zinc Loss in the Microwave Dielectric Oxide $Ba_{3}ZnTa_{2}O_{9-{\delta}}$," Chem. Mater., 15 (2), pp. 586-597, 2003. https://doi.org/10.1021/cm020461e
  5. Hiroyuki Matsumoto, Hiroshi Tamura and Kikuo Wakino, "$Ba(Mg, Ta)O_{3}-BaSnO_{3}$ High-Q Dielectric Resonator, Jpn. J. Appl. Phys. 30, pp. 2347-2349, 1991. https://doi.org/10.1143/JJAP.30.2347
  6. Cristina Jinga, Daniela Berger, Cristian Matei, Sorin Jinga, Ecaterina Andronescu, "Characterization of $BaMg_{1/3}(Ta_{1-x}Nbx)_{2/3}O_{3}$ ceramics obtained by a modified Pechini method," Journal of Alloys and Compounds 497(1-2), pp. 239-243, 2010. https://doi.org/10.1016/j.jallcom.2010.03.019
  7. Hao Zhuang, Zhenxing Yue, Siqin Meng, Fei Zhao, Longtu Li, "Low-temperature sintering and microwave dielectric properties of $Ba_{3}(VO_{4})_{2}-BaWO_{4}$ ceramic composites", J. Am. Ceram. Soc. 91, pp. 3738-3741, 2008. https://doi.org/10.1111/j.1551-2916.2008.02672.x
  8. J. R. Yoon, D. S. Shin, D. Y. Jeong, and H.Y Lee, "Control of connectivity on Ni electrode with heating rates during sintering and electrical properties in $BaTiO_{3}$ based multilayer ceramic capacitors" Trans. Electr. Electron. Mater. 13(4), pp. 181 -184, 2012. https://doi.org/10.4313/TEEM.2012.13.4.181
  9. Dae-Yong Jeong, Soon-il Lee, Heun-Young Lee, Min-Kee Kim and Jung-Rag Yoon, "Electrical Properties of $BaTiO_{3}$-Based Multilayer Ceramic Capacitors Sintered with Plasma-Treated Glass Powder," Jpn. J. Appl. Phys. 52, 2013.
  10. D. Kajfez, S.Chebolu, M.R.Abdul-Gaffoor, and A. A. Kishk, "Uncertainty analysis of the transmission-type measurement of Q-factor", IEEE Transactions on Microwave Theory and Techniques 47, pp. 367-731, 1999. https://doi.org/10.1109/22.750244
  11. Jung-Rag Yoon, Jung-Yul Kwon, and Heun-Yong Lee, "The microwave measurement of the dielectric properties by the parallel plate resonator and ceramic cavity method", Properties and Applications of Dielectric Materials, 1997., Proceedings of the 5th International Conference on (Volume:2 ), 1997.