Bloating mechanism for coal ash with iron oxide

철분이 많이 함유된 석탄회의 발포거동

  • Lee, Ki Gang (Department of Advanced Material Science and Engineering, Kyonggi University)
  • Received : 2014.03.07
  • Accepted : 2014.04.04
  • Published : 2014.04.30

Abstract

The purpose of this study was to figure out the impacts of iron oxide types and dosages to bloating when producing artificial lightweight aggregates by utilization of recycled resources such as bottom-ash, reject-ash and dredgedsoil. In order to figure out chemical characteristics of raw materials, XRD and XRF analyses were performed. 50 wt% of dredged-soil, 15 wt% of bottom-ash and 35wt.% of reject-ash were mixed, then the amount of iron oxide was varied at 5 to 30 wt% with intervals of 5 wt% with $Fe_2O_3$ and $Fe_3O_4$ respectively. As molded aggregates were sintered by rapid sintering in intervals of $40^{\circ}C$ from $1060^{\circ}C$ to $1180^{\circ}C$, specific gravity and water absorption were measured. As a result, the artificial lightweight aggregate with iron oxide of 10~15 vol% showed the lowest specific gravity, and it was identified that the more iron oxide vol% increases, the more specific gravity increases because of liquid phase sintering.

본 연구는 순환자원인 저회, 잔사회 그리고 준설토로 인공 경량골재를 제조할 때 철분의 종류와 양이 발포기구에 미치는 영향을 분석하는 것이다. 원료의 화학적 특성을 X선 회절 분석과 X선 형광 분석으로 측정하였다. 준설토 50 %, 저회 15 % 그리고 잔사회 35 %를 무게비로 혼합하고 철분함량을 5 % 단위로 30 %까지 첨가하였으며, 철분의 종류는 $Fe_2O_3$$Fe_3O_4$로 선정하였다. 성형된 골재는 급속 소성법으로 $40^{\circ}C$ 간격으로 $1060^{\circ}C$에서 $1180^{\circ}C$까지 소결하고, 비중과 흡수율을 측정하였다. 인공 경량골재는 철분 함유량이 10~15 %일 때 가장 낮은 비중을 보이며, 철분량이 증가할수록 액상 소결이 되어 비중이 증가하였다.

Keywords

References

  1. Ministry of Knowledge Economy, "The 5th Basic plan for Long-term Electricity Supply and Demand" (2010-2024).
  2. E. Berg and J.A. Neal, "Concrete masonry unit mix designs using municipal solid waste bottom ash", ACI Materials Journal 95 (1998) 470.
  3. K.G. Lee, "Bloating mechanism of artificial lightweight aggregate with reject ash", J. Korean Cryst. Growth Cryst. Technol. 22 (2012) 158. https://doi.org/10.6111/JKCGCT.2012.22.3.158
  4. K.D. Kim, J.H. Kim, Y.T. Kim, S.G. Kang and K.G. Lee, "Production of lightweight aggregates using power plant reclaimed ash", J. Korean Cryst. Growth Cryst. Technol. 19 (2009) 318.
  5. S.J Kumar and J. Stewart, "Evaluation of illinois pulverized coal combustion dry bottom ash for use in geotechnical engineering application", J. Energy Eng. 129 (2003) 42. https://doi.org/10.1061/(ASCE)0733-9402(2003)129:2(42)
  6. Omer Ozkan, Isa Yukel and Ozgur Muratoglu, "Strength properties of concrete incorporating coal bottom ash and granulated blast furnace slag," Waste Management 27 (2007) 161. https://doi.org/10.1016/j.wasman.2006.01.006
  7. L.B. Andrade, J.C. Rocha and M. Cheriaf, "Influence of coal bottom ash as fine aggregate on fresh properties of concrete," Construction Buil. Mater. 23 (2007) 609.
  8. KS F 4570 : Bottom ash aggregate for the precast concrete product (2007).
  9. KS F 4569 : Bottom ash aggregate for road construction (2007).
  10. S.H. Kang and K.G. Lee, "Bloating mechanism of artificial lightweight aggregate for recycling the waste glass", J. Kor. Cer. Soc. 47 (2010) 445. https://doi.org/10.4191/KCERS.2010.47.5.445
  11. Y.T. Kim, Y.G. Ryu, C.S. Jang, K.G. Lee, S.G. Kang and J.H. Kim, "A study on the black core formation of artificial lightweight aggregates at various sintering atmosphere", J. Korean Cryst. Growth Cryst. Technol. 19 (2009) 318.
  12. S.H. Knag, K.G. Lee and Y.T. Kim, "Effects of chemicophysical properties of carbon on bloating characteristics of artificial lightweight aggregates using coal ash", Ceramic Transactions 232 (2012) 35.
  13. J. Park, Y. Kim and Y. Choi, "Property enhancement of lightweight aggregate by carbonation processing", J. Korean Cryst. Growth Cryst. Technol. 22 (2012) 254. https://doi.org/10.6111/JKCGCT.2012.22.5.254
  14. K. Kim and S. Kang, "Characterization of artificial aggregates of coal bottom ash-red clay system", J. Korean Cryst. Growth Cryst. Technol. 22 (2012) 305. https://doi.org/10.6111/JKCGCT.2012.22.6.305
  15. J. Letsch and W. Noll, "Phase formation in several ceramics subsystems at $600^{\circ}C{\sim}1000^{\circ}C$ as a function of oxygen fugacity", cfi/Ber. DKG 7 (1983) 259.

Cited by

  1. Study on the prevention methods of radial cracks generated in artificial lightweight aggregate vol.25, pp.5, 2015, https://doi.org/10.6111/JKCGCT.2015.25.5.199
  2. Study on the control of marine biofouling developed on the surface of porous ceramics vol.25, pp.5, 2015, https://doi.org/10.6111/JKCGCT.2015.25.5.218
  3. Bloating Mechanism for Artificial Light Weight Aggregate of Surface Modification with Coal ash vol.52, pp.2, 2015, https://doi.org/10.4191/kcers.2015.52.2.159