AC2B 알루미늄 주조합금의 응고균열 강도에 미치는 금형 예열온도의 영향

Effect of Mold Preheat Temperature on Solidification Crack Strength of AC2B Aluminum Alloy

  • 김헌주 (부경대학교 공과대학 금속공학과)
  • Kim, Heon-Joo (Dept. of Metallurgical Eng., Pukyong National Univ.)
  • 투고 : 2014.07.23
  • 심사 : 2014.10.17
  • 발행 : 2014.10.31

초록

The effect of the mold preheat temperature on the solidification crack strength was investigated in AC2B aluminum alloy. A tension type apparatus as part of a solidification crack test which could measure the stress-strain relationship quantitatively was utilized. The evaluation of the solidification crack strength with varying mold preheat temperatures was performed by the test procedure established in this research. When the mold preheat temperatures were $250^{\circ}C$, $150^{\circ}C$ and $50^{\circ}C$, the solidification crack strengths were found to be $7.8Kgf/cm^2$, $12.9Kgf/cm^2$ and $28.6Kgf/cm^2$, respectively. In the same way, when the mold preheat temperatures were $250^{\circ}C$, $150^{\circ}C$ and $50^{\circ}C$, the corresponding temperatures of the failure sites were $610^{\circ}C$, $600^{\circ}C$ and $571^{\circ}C$, and the calculated solid fractions were 14.0%, 29.3% and 50.8% when the specimens failed, respectively. The solidification crack strength increased in proportion to the solid fraction of the failure site. The solidification crack strength obtained in this test is assumed to reflect the effects of metallurgical factors on the thermo-plastic characteristics of a solidifying alloy such as the grain size of the solid, the grain morphology, and the distribution of solid grain.

키워드

참고문헌

  1. Jorstad J. L, Die Casting Engineer, "Future technology in Aluminum die casting", 9 (2006) 18-25.
  2. Trenda G, Cast Plant Technol., "Die casting alloy for ductile thin-walled Structural Parts", 22 (2006) 28.
  3. Sigworth G. K, Koch H and Krug P, Light Metals Symposium in Proceedings of the 40th-Annual Conference of Metallurgist and Electrometallurgy, "High Strength natural aging aluminum casting alloys for automotive applications", Toronto, Canada, August 26-29 (2001) 349-358.
  4. Koch H and Franke A. J, Transaction of the 20th International Die Casting Congress and Exposition, "Development of a super ductile high pressure die casting alloy for crash relevant parts", Cleveland, OHIO, Nov., (1999) 11-14.
  5. Watanabe T, Kimura R, Nakazawa T, Chiba H, Tanaka S, Ueki T, Toriyama T and Yoshida M, J. of Japan Institute of Light Metals, "Development of the theories of solidification cracking and measuring methods for mechanical properties of solidliquid coexistence alloys", 58 (2008) 395-405. https://doi.org/10.2464/jilm.58.395
  6. Clyne T. W and Davies G. J, Proc. Conf. on Solidification and Casting of Metals, "Solidification and casting of metals", (1979) 275.
  7. Metz A. S and Flemings M. C, AFS Trans., "A Fundamental Study of Hot Tearing" 78 (1970) 453-460.
  8. Sequeria W, Pikhovich V and Weiss D, Modern Casting "Finding new strength in Aluminum", Feb., (2006) 36-41.
  9. Spittle A and Cushway A. A, Met., Technol., "Influence of Superheat and Grain Structure on Hot Tearing Susceptibilities of Al-Cu alloy Castings", 10 (1983) 6-13. https://doi.org/10.1179/030716983803291226
  10. Instone S, StJohn D and Grandfield J, International Journal of Cast Material Research, "New apparatus for characterising tensile strength development and hot cracking in the mushy zone", 12 (2000) 441-456.
  11. Kim HJ, Journal of Korea Foundry Society, "Quantitative Evaluation of Solidification Crack Strength of AC2B Aluminum Casting Alloy", 8 (2014) 248-254.
  12. Jorstad J. L, Wayne and Zalensas D. L, Aluminum Casting Technology 2nd Edi., American Foundrymen's Society Inc., (1997) 21-26.
  13. Viano D, StJohn D, Grandfield J and Caceres C, Light Metals 2005, "Hot Tearing in Aluminium-Copper Alloys" (2005) 1069-1073.
  14. Fjaer H. G and Mo A, Metall. Meter. Trans. B, "A mathematical model for thermal stresses in direct chill casting of Aluminium billets", 21B (1990) 1049-1061.
  15. Magnin B, Katgerman L and Hannart B, Proc. 7th Conf. Modelling of Casting, Welding and advanced solidification processes, VII, Edit by X. M. Cross and J. Campbell, "Physical and numerical modelling of thermal stress generation during DC casting of Aluminum alloys", Warrendale, PA, USA, (1995) 303-310.
  16. Lahaie D. J and Bouchard M, Metall. Meter. Trans. B, "Physical modeling of the deformation mechanisms of semisolid bodies and a mechanical criterion for hot tearing", 32B (2001) 697-705.
  17. Prokhorov N. N, Russian Castings Production, "Re nement in the hot tearing of cast Al-Cu alloy", 2 (1962) 172-175.
  18. Rappaz M, Drezet J.-M and Gremaud M, Metall. Meter. Trans. A, "A new hot-tearing criterion", 30A (1999) 449-455.
  19. Eskin D. G and Katgerman L, Metall. Meter. Trans. A, "A quest for a new hot-tearing criterion", 38A (2007) 1511-1519.
  20. Dahle A. K, Instone S and Sumitomo T, Metallurgical and Materials Transaction A, "Relationship between Tensile and Shear Strengths of the Mushy Zone in Solidifying Aluminum Alloys", 34A(2003) 105-113.

피인용 문헌

  1. Effect of Scrap Content on the Hot Tearing Property and Tensile Property of AC2BS Alloy vol.36, pp.2, 2016, https://doi.org/10.7777/jkfs.2016.36.2.67
  2. AC4A 알루미늄 합금의 주조특성에 미치는 미량 첨가원소의 영향 vol.37, pp.5, 2017, https://doi.org/10.7777/jkfs.2017.37.5.148