Abstract
The Sr based ceramic thin films were deposited on Si substrate by RF magnetron sputtering method. And Sr based thin films were annealed at $500{\sim}700^{\circ}C$ using RTA. The surface roughness showed about 2.4 nm in annealed thin film at $600^{\circ}C$. The capacitance density of Sr based thin films were increased with the increase of annealing temperature. The maximum capacitance density of $0.6{\mu}F/cm^2$ was obtained by annealing temperature at $700^{\circ}C$. The voltage dependence of dielectric loss showed about 0.02 in voltage ranges of -10~+10 V. The leakage current density of annealing temperature of $600^{\circ}C$ was the $4.0{\times}10^{-6}\;A/cm^2$ at applied voltage of -5~+5 V.