Abstract
This study was carried out to investigate the possibility of using basalt powder sludge instead of sand in a normal cement dry mortar as a way to recycle basalt powder sludge, which is a waste product from the manufacturing a process of basalt in Jeju. Basic performance evaluations of the dry mortar material included a compressive strength test, a flexural strength test, and SEM to observe the micro structure. The compressive and flexural strengths were increased to a replacement ratio of 21% of basalt powder sludge, whereby a strength enhancement of about 40% greater than that of normal dry mortar was shown. However, the creation of hydration products affected the replacement ratio of the basalt powder sludge. The possibility of using basalt powder sludge waste was identified in this study, and results showed that the basalt powder sludge waste could be used as a material for a secondary product of concrete.
본 연구는 최근 제주도 지역에서 현무암 가공과정에서 발생되는 폐기물인 석분슬러지를 재활용하기 위한 방안으로써 일반 시멘트몰탈에 사용되는 잔골재 대신에 현무암 석분슬러지의적용가능성에 대해 실험하였다. 드라이 몰탈의 재료로서의 기초적인 성능을 평가하기 위해 압축강도와 휨강도를 평가하고, SEM을 통해 미세구조를 관찰하였다. 현무암 슬러지 대체율 21%까지는 압축 및 휨강도는 증가하였으며, 보통 드라이몰탈보다 약 40% 강도 증진 효과가 있다. 현무암 슬러지의 대체율 약 20%이상에서는 상대적으로 수화생성물이 적게 생성되었다. 본 연구를 통해 현무암 슬러지 폐기물의 활용성을 확인할 수 있었으며, 콘크리트 2차 제품의 성형에도 가능할 것으로 판단된다.