Abstract
In this study, Fe-base alloy powder was prepared by gas atomizing method. Shape and crystal structure of the powder were investigated by FESEM, X-ray diffraction, and DSC. The powder was produced in a spherical shape, with a size of 45 ~ 90 ${\mu}m$. X-ray diffraction analysis revealed that the powder was fully amorphous, showing typical broad amorphous peak. From DSC analysis, Tg and Tx that are generally found in a bulk amorphous alloy were also observed in the alloy powder. Tg and Tx of the powder were $530^{\circ}C$ and $560^{\circ}C$, respectively. These results suggest us that the bulk amorphous alloy (BMG) powder prepared in this study is applicable to laser welding.
본 연구에서는 가스아토마이저를 이용하여 Fe계 비정질 합금 분말을 제조하였고, 제조된 비정질 분말의 특성을 평가하였다. Fe계 비정질 합금분말의 형상, 결정구조, 비정질 형성능 분석은 고분해능 주사전자현미경(FESEM), X-선 회절분석기, 시차주사열량측정법(DSC)을 이용하여 각각 분석하였다. 분말은 45~90 ${\mu}m$ 크기의 구형으로 생성되었다. 제조된 Fe-계 합금분말을 X-선 회절 분석한 결과 결정피크는 관찰되지 않고 전형적인 비정질 결정구조 피크만 관찰되었다. 합금분말의 DSC 분석결과 벌크비정질합금에서 나타나는 Tg와 Tx가 존재하였으며, Tg = $530^{\circ}C$, Tx = $560^{\circ}C$로 관찰되었다. 이러한 결과로부터 본 연구를 통하여 제조된 구형의 벌크비정질합금(BMG) 분말은 레이저 용접에 적용이 가능한 재료임을 알 수 있었다.