An Experimental Study on the Carbonation and Drying Shrinkage of Concrete Using High Volumes of Ground Granulated Blast-furnace Slag

고로슬래그 미분말을 대량 사용한 콘크리트의 건조수축 및 중성화에 관한 실험적 연구

  • Received : 2012.01.26
  • Accepted : 2012.06.11
  • Published : 2012.08.20

Abstract

The effect of ground granulated blast-furnace slag (GGBS) and alkaline activator on the properties of setting, compressive strength, drying shrinkage and resistance of carbonation was assessed to develop high volume slag concrete, the GGBS replacement rate of which was more than 80 percent. The changes in the concrete as the replacement rate of GGBS increases were as follows. Initial and final setting time was delayed by two and a half hours, and the compressive strength development properties of concrete in early and long term age were decreased. Drying shrinkage was satisfactory as below $6{\times}10^{-4}$ in every mixture, and yet showed a tangible trend by replacement rate. Carbonation was materially increased. Setting time and early strength development property, however, were extremely advanced by the addition of the alkaline activator. While drying shrinkage was improved by the alkaline activator, resistance to carbonation was not.

본 연구에서는 고로슬래그의 치환율이 80% 이상에 이르는 슬래그 대량 치환 콘크리트(High Volume Slag Concrete, HVSC)의 개발을 목표로 응결특성, 압축강도, 건조수축 및 중성화 저항성에 미치는 고로슬래그 치환율의 영향 및 알칼리 자극제의 효과에 대해 평가하였다. 고로슬래그 미분말의 치환율 증가에 따른 시험결과는 다음과 같다. 응결시간은 초결 및 종결 도달시간이 약 2~2.5 시간 지연되는 것으로 나타났으며 압축강도 발현특성은 초기 및 장기의 모든 재령에서 감소하였다. 건조수축은 치환율에 따른 뚜렷한 경향을 나타내지 않았으며 모든 배합에서 $6{\times}10^{-4}$ 이하의 값을 보여 매우 양호한 것으로 나타났다. 중성화는 현저히 증가하는 경향을 나타냈다. 한편 알칼리 자극제의 첨가에 따른 응결시간 및 초기강도 발현특성은 현저히 개선되었으며 건조수축에 기여하는 효과가 큰 것으로 나타났다. 반면 중성화 저항성에 미치는 영향은 크지 않은 것으로 나타났다.

Keywords

References

  1. Ferraris CF, Obla KH, Hill R. The influence of mineral admixtures on the rheology of cement paste and concrete. Cement and Concrete Research. 2001;31(2):245-55. https://doi.org/10.1016/S0008-8846(00)00454-3
  2. Chan WWJ, Wu CML. Durability of concrete with high cement replacement. Cement and Concrete Research. 2000;30(6):865-79. https://doi.org/10.1016/S0008-8846(00)00253-2
  3. Domone PL, Soutsos MN. Properties of high-strength concrete mixes containing PFA and ggbs. Magazine of Concrete Research. 1995;47(173):355-67. https://doi.org/10.1680/macr.1995.47.173.355
  4. Hester D, McNally C, Richardson MG. A study of influence of slag alkali level on the alkali-silica reactivity of slag concrete. Construction and Building Materials. 2005;19(9):661-5. https://doi.org/10.1016/j.conbuildmat.2005.02.016
  5. Leng F, Feng N, Lu X. An experimental study on the properties of resistance to diffusion of chloride ions of fly ash and blast furnace slag concrete. Cement and Concrete Research. 2000;30(6):989-92. https://doi.org/10.1016/S0008-8846(00)00250-7
  6. Architectural Institute of Japan. Recommendation for Practice of Concrete with Portland Cement and Ground Granulated Blast-Furnace Slag. Tokyo (Japan): Architectural Institute of Japan; 2001. p. 35-52.
  7. Lee SS, Song HY. An experimental study on the durability and mechanical properties of high performance concrete using blast-furnace slag powder. Journal of Architectural Institute of Korea. 2007 Nov.;23(11):119-26.
  8. Sagawa T, Nawa T. Hydration microstructural evolution and drying shrinkage of portland cement - blast furnace slag system. Journal of Structural and Construction Engineering. AIJ. 2010 Jun.;75(652):1029-37. https://doi.org/10.3130/aijs.75.1029
  9. Li C, Yoda A, Yokomuro T. Effect of ground granulated blast furnace slag on pore structure and compressive strength of hardened cement pastes. Journal of Structural and Constrution Engineering. AIJ. 1998 April;506:1-6.
  10. Oner A, Akyuz S. An experimental study on optimum usage of GGBS for the compressive strength of concrete. Cement and Concrete Composite. 2007 January;29(6):505-14. https://doi.org/10.1016/j.cemconcomp.2007.01.001
  11. Hwang CL, Lin CY. Strength development of blended blast furnace slag cement mortars. ACI SP 91-65, Detroit. 1986;91:1323-40.
  12. McNally C., Sheils E. Probability-based assessment of the durability characteristics of concretes manufactured using CEM II and GGBS binders. Construction and Building Materials. 2012;30:22-9. https://doi.org/10.1016/j.conbuildmat.2011.11.029
  13. Nagashio Y., Masuda Y. Influence of ground granulated blast-furnace slag on drying shrinkage and cabonation of concrete with ecocement. Journal of Structural and Construction Engineering: Transactions of AIJ. 2010 April;75(650):675-80. https://doi.org/10.3130/aijs.75.675
  14. Jianyong L, Yan Y. A study on creep and drying shrinkage of high performance concrete. Cement and Concrete Research. 2001;31(8):1203-06. https://doi.org/10.1016/S0008-8846(01)00539-7
  15. Richardson I.G. Tobermorite/jennite- and tobermorite/ calcium hydroxide-based models for the structure of C-S-H: applicability to hardened pastes of tricalcium silicate, ${\beta}$ -dicalcium silicate, Portland cement, and blends of Portland cement with blast-furnace slag, metakaolin, or silica fume. Cement and Concrete Research. 2004;34(9):1733-77. https://doi.org/10.1016/j.cemconres.2004.05.034
  16. Bakharey T, Sanjayan JG, Cheng Y-B. Resistance of alkali-activated slag concrete to carbonation. Cement and Concrete Research. 2001;31(9):1277-83. https://doi.org/10.1016/S0008-8846(01)00574-9

Cited by

  1. Effect of Fine Particle Cement and Recycled Aggregates as Alkali Activator on the Engineering Properties and Micro-Structure of High Volume Blast Furnace Slag Concrete vol.13, pp.6, 2013, https://doi.org/10.5345/JKIBC.2013.13.6.602
  2. Effect of Emulsified Refine Cooking Oil and Expandable Microsphere on Durability of High-Volume Blast Furnace Slag Concrete vol.15, pp.2, 2015, https://doi.org/10.5345/JKIBC.2015.15.2.201
  3. A study of the effect of light-burnt dolomite on the hydration of alkali-activated Portland blast-furnace slag cement vol.57, 2014, https://doi.org/10.1016/j.conbuildmat.2014.01.071
  4. Shrinkage Properties and Potential for Cracking of High-strength Concrete containing High-volume Blast Furnace Slag vol.31, pp.6, 2015, https://doi.org/10.5659/JAIK_SC.2015.31.6.51
  5. Comparative studies on the effects of sewage sludge ash and fly ash on cement hydration and properties of cement mortars vol.154, 2017, https://doi.org/10.1016/j.conbuildmat.2017.08.003
  6. Effects of Limestone Powder and Silica Fume on the Hydration and Pozzolanic Reaction of High-Strength High-Volume GGBFS Blended Cement Mortars vol.27, pp.2, 2015, https://doi.org/10.4334/JKCI.2015.27.2.127
  7. Durability Performance of Concrete using Rice Husk Ash vol.13, pp.2, 2013, https://doi.org/10.5345/JKIBC.2013.13.2.139
  8. An Experimental Study on the Chloride Attack Resistibility of Alkali-Activated Ternary Blended Cement Concrete vol.16, pp.4, 2016, https://doi.org/10.5345/JKIBC.2016.16.4.321
  9. Preventing Carbonation of High-volume SCM Concrete by Painting Emulsified Refined Cooking Oil vol.31, pp.11, 2015, https://doi.org/10.5659/JAIK_SC.2015.31.11.55
  10. Effects of Replacement Ratio and Fineness of GGBFS on the Hydration and Pozzolanic Reaction of High-Strength High-Volume GGBFS Blended Cement Pastes vol.27, pp.2, 2015, https://doi.org/10.4334/JKCI.2015.27.2.115
  11. Properties of the Alkali Activated Mortar According to Metakaolin Replacement Ratio vol.16, pp.4, 2016, https://doi.org/10.5345/JKIBC.2016.16.4.313
  12. Mercury intrusion porosimetry characterization of micropore structures of high-strength cement pastes incorporating high volume ground granulated blast-furnace slag vol.137, 2017, https://doi.org/10.1016/j.conbuildmat.2017.01.076
  13. Strength Development and Durability of High-Strength High-Volume GGBFS Concrete vol.3, pp.3, 2015, https://doi.org/10.14190/JRCR.2015.3.3.261
  14. Effect of Powder Hardening Accelerator on the Physical Properties of Precast Concrete vol.15, pp.3, 2015, https://doi.org/10.5345/JKIBC.2015.15.3.265
  15. An Experimental Study on Early Strength and Drying Shrinkage of High Strength Concrete Using High Volumes of Ground Granulated Blast-furnace Slag(GGBS) vol.13, pp.4, 2013, https://doi.org/10.5345/JKIBC.2013.13.4.391
  16. Influence of Painting Materials based on Wasted Oil and Applying Timing on Carbonation and Chloride Resistances of High Volume SCM Concrete vol.3, pp.3, 2015, https://doi.org/10.14190/JRCR.2015.3.3.228
  17. A Study on the Development of Non-PC High-Early-Strength Concrete Without Steam Curing vol.14, pp.2, 2014, https://doi.org/10.5345/JKIBC.2014.14.2.156
  18. The Reduction of Maximum Hydration Temperature in Cement Paste Using Calcium Silicate Hydrates and Glucose vol.27, pp.3, 2015, https://doi.org/10.4334/JKCI.2015.27.3.265
  19. Evaluating Strength Development and Durability of High-Strength Concrete with 60% of Ground-Granulated Blast Furnace Slag vol.18, pp.7, 2018, https://doi.org/10.9798/KOSHAM.2018.18.7.307