A Study on the Carbonation Characteristics of ALC

ALC의 탄산화 특성에 관한 연구

  • Seo, Sung Kwan (Energy & Environment Div., Korea Institute of Ceramic Eng. & Tech.) ;
  • Chu, Yong Sik (Energy & Environment Div., Korea Institute of Ceramic Eng. & Tech.) ;
  • Park, Soo Hyun (Energy & Environment Div., Korea Institute of Ceramic Eng. & Tech.) ;
  • Song, Hun (Energy & Environment Div., Korea Institute of Ceramic Eng. & Tech.) ;
  • Lee, Jong Kyu (Energy & Environment Div., Korea Institute of Ceramic Eng. & Tech.)
  • 서성관 (한국세라믹기술원 에너지환경소재본부) ;
  • 추용식 (한국세라믹기술원 에너지환경소재본부) ;
  • 박수현 (한국세라믹기술원 에너지환경소재본부) ;
  • 송훈 (한국세라믹기술원 에너지환경소재본부) ;
  • 이종규 (한국세라믹기술원 에너지환경소재본부)
  • Received : 2012.10.19
  • Accepted : 2012.10.29
  • Published : 2012.10.31
Download PDF
⟨ Previous Next ⟩

Abstract

For Analysis and evaluation of ALC carbonation, ALC with various specific gravity was fabricated and silicate and siloxane were used for spraying on ALC surface. Silicon oil of water repellent was added to ALC slurry. ALC carbonation related with specific gravity and carbonation degree was decreased with specific gravity. It was guessed that permeation of $CO_2$ gas reduced depend on compact structure of ALC. ALC which sprayed silicate and siloxane represented more excellent carbonation resistance than Ref. ALC. ALC added silicon oil represented most excellent carbonation resistance.

ALC의 탄산화를 분석 평가하기 위하여 비중을 0.4, 0.5 및 $0.7g/cm^3$로 제어하였으며, 이중 $0.5g/cm^3$ ALC에 실리케이트 및 실록산계 발수제를 표면 도포하였다. 또한 슬러리에 실리콘 오일 발수제를 첨가하여 ALC를 제조하기도 하였다. ALC의 탄산화는 비중과 밀접한 관련이 있었으며, ALC의 비중이 높아짐에 따라 탄산화도는 감소하였다. 이는 ALC 조직이 치밀할수록 $CO_2$ 가스의 침투가 어려워지기 때문이다. 실리케이트 및 실록산계 발수제를 표면 도포한 ALC에서는 Ref. ALC 보다 탄산화 저항성이 우수하였다. 또한 슬러리에 실리콘 오일을 첨가한 ALC에서 가장 우수한 탄산화 저항성을 나타내었다.