Abstract
The damage analysis method in this paper needs a material property and failure criteria. The material properties and the failure criteria could be easily obtained from the results of notched bar tensile tests carried out on other materials studied previously. However, for the cast stainless steel (CF8M) material in this paper, because of the variance in the results from notched bar tensile tests under the same conditions, the material property and the failure criteria could be obtained differently, depending on the analyzer. Therefore, a proper procedure that can confirm the material property and failure criteria are needed. In this work, the averaged material property was obtained from the notched bar with a 16-mm notch radius, and three failure criteria for CF8M material by finite element analysis were obtained. Applying the material property and the failure criteria, FE damage analysis for the J-R fracture toughness test was conducted. For validation, the simulated results were compared with the experimental results.
본 논문의 유한요소 손상해석기법은 재료 인장물성과 파괴기준을 필요로 한다. 기존에 연구된 재료들은 노치인장 시험결과로부터 하나의 인장물성과 파괴기준을 구할 수 있었다. 그러나 본 논문에서 사용된 cast stainless steel(CF8M)의 경우, 동일한 조건의 노치인장 시험결과들에 분산이 존재하여 해석자에 따라 다른 인장물성과 파괴기준이 구해질 수 있다. 따라서 해석자에 관계없이 일관된 인장물성 및 파괴기준을 구할 수 있는 적절한 절차가 필요하다. 본 논문에서는 노치반경 16mm 의 인장시편 시험결과로부터 평균 인장물성을 구하였고, 이를 유한요소 해석에 적용하여 3 개의 파괴기준을 구하였다. 구해진 인장물성과 파괴기준을 적용하여 J-R 파괴인성 시험에 대한 손상해석을 수행하였고, 시험결과와 비교함을 통해 제시된 절차의 타당성을 검증하였다.