The characteristics of Al-doped ZnO films deposited with RF magnetron sputtering system in various H₂/(Ar+H₂) gas ratios

The properties of Al-doped ZnO (AZO) films were investigated as a function of H2/(Ar + H2) gas ratio using an AZO (2 wt% Al2O3) ceramic target in a radio frequency (RF) magnetron sputtering system. The deposition process was done at 200 ℃ and in 2 × 10-2Torr working pressure and with various ratios of H2/(Ar + H2) gas. During the AZO film deposition process, partial H2 gas affected the AZO film characteristics. The electron resistivity (~ 9.21 × 10-4 Ωcm) was lowest and mobility (~17.8 ㎠/Vs) was highest in AZO films when the H2/(Ar + H2) gas ratio was 2.5%. When the H2/(Ar + H2) gas ratio was increased above 2.5%, the electron resistivity increased and mobility decreased with increasing H2/(Ar + H2) gas ratio in AZO films. The carrier concentration increased with increasing H2/(Ar + H2) gas ratio from 0% to 7.5%. This phenomenon was explained by reaction of hydrogen and oxygen and additional formation of oxygen vacancy. The average optical transmission in the visible light wavelength region over 90% and an orientation of the deposition was [002] orientation for AZO films grown with all H2/(Ar + H2) gas ratios.