Abstract
The purpose of this study was to investigate the influence of recycled aggregates powder (RP) contents on recycled aggregates (RA) using fly-ash (FA) mortar in a condition of zero cement targeting earth filling materials, and the results can be summarized as follows. First, there was a tendency that as RP contents increased, W/B and air contents increased also. In the case of compressive strength, the strength was hardly developed at the early age, which was prior to 14 days; however, with the starting point of 14 days of age, strength of around 1.5~2.0 MPa was developed when it arrived at 28 days. At a curing temperature of $20^{\circ}C$, the more RP contents increased, the more the compressive strength increased in comparison with FA 100% at all levels except RP 100 %, showing the highest compressive strength at RP 25 %. At a curing temperature of $35^{\circ}C$, the temperature-dependence appeared to be large, as the RP contents were decreased compared to the curing temperature of $20^{\circ}C$. In addition, based on SEM analysis, this study was able to confirm that a pozzolanic reaction formed by an alkali stimulus of RA with the lapse of certain days even in 100 percent FA, causing the densification of tissues, and with RP 25%, hydrate was created the most densely by the hydration of unhydrated cement particles and pozzolanic reaction of FA.
본 연구는 지반매립재 용도를 대상으로 무 시멘트 상태에서, RA 사용 FA 모르타르의 특성에 미치는 RP 치환율의 영향을 검토하였는데, 그 결과를 요약하면 다음과 같다. 먼저, W/B 및 공기량은 RP 치환율이 증가할수록 증가하는 경향을 나타내었다. 압축강도는 재령 14일 이전 초기 재령에서는 강도가 거의 발휘되지 못하였으나, 재령 14일을 기점으로 28일에 이르러서는 약 1.5~2.0 MPa 정도의 강도 값을 나타내었다. 양생온도 $20^{\circ}C$의 경우 RP 치환율 100 %를 제외한 모든 수준에서 순수 FA에 비해 RP 치환율이 증가할수록 강도는 증가하였는데, RP 25 %에서 최고 강도값을 나타내었다. 양생온도 $35^{\circ}C$에서는 $20^{\circ}C$보다 RP 치환율이 작을수록 온도의존성이 큰 것으로 나타났다. 한편, SEM분석결과, 순수 FA에서도 일정 재령이 경과하면 RA의 알칼리 자극으로 포졸란 반응이 생성되어 조직이 치밀화됨을 확인할 수 있었고, RP 치환율 25 %일 때 RP의 미수화 시멘트 입자의 수화 및 FA의 포졸란 반응으로 수화물이 가장 밀실하게 생성되었다.