Thermoluminescence Properties of Elpasolite Scintillation Single Crystal

엘파소라이트 섬광형 단결정의 열형광 특성

In this paper, we determined the scintillation and thermoluminescence properties of $Cs_2NaCeBr_6$ elpasolite scintillation crystal. The emission spectrum of $Cs_2NaCeBr_6$ is located in the range of 300 ~ 450 nm, peaking at 377 nm and 400 nm. And, the fluorescence decay time of the crystal is composed two components. The fast component is 140 ns (94%), and the slow component is 880 ns (6%) of the crystal. The after-glow is caused by the electron and hole traps in the crystal lattices. We determined thermoluminescence parameters of the traps in the crystal. The determined activation energy(E), kinetic order and frequency factor of the traps are 0.67 eV, 1.71 and $2.51{\times}10^8s^{-1}$ respectively. In this crystal, re-combination rate is more dominant phenomenon than the re-trapping rate.

본 논문에서는 $Cs_2NaCeBr_6$ 엘파소라이트 단결정의 섬광 및 열형광 특성에 대하여 조사하였다. $Cs_2NaCeBr_6$의 형광스펙트럼은 $Ce^{3+}$ 이온의 $4f{\rightarrow}5d$ 천이에 따라 파장범위가 300 ~ 450 nm, 피이크 파장은 377 nm 및 400 nm이었다. 형광감쇠시간 특성은 140 ns의 빠른 시간 특성 성분(94%)과 880 ns의 느린 성분(6%)의 2개로 구성된다. 잔광에 기여한 포획준위의 물리적 변수를 열형광측정법에서 측정한 결과, 포획준위의 활성화에너지, 발광차수 및 주파수 인자는 각각 0.67 eV, 1.71 및 $2.51{\times}10^8s^{-1}$이었으며, 이는 여기된 전자의 재포획율보다는 재결합율이 더 우세하기 때문인 것으로 사료된다.