The Effect of Mixing Ratio of Blast Furnace Slag and Fly Ash on Material Properties of 80MPa High Strength Concrete with Ternary Cement

고로슬래그와 플라이애시 대체율이 80MPa 3성분계 고강도콘크리트의 재료물성에 미치는 영향

To develop 80MPa-high strength concrete with ternary cement used in OPC, blast-furnance slag, and fly ash, mixing ratio of blast-furnace slag and fly ash was evaluated in material characteristics before and after hardening of the high strength concrete. According to the evaluated results of material characteristics before and after hardening of the high strength concrete, the flowability and long-term compressive strength increase up to 30% mixing ratio of blast-furnace slag and fly ash. Also, it is superior to characteristics of length change and neutralization due to the use of mineral admixture when compared in test sample mixed with OPC. The evaluated results show that material characteristics of the high strength concrete was the most outstanding performance at blast-furnace slag of 25% and fly ash of 15%. The result of this study will be useful for the development of high strength concrete as a substitute of costly silica fume in the near future.

보통포틀랜드시멘트(OPC)와 고로슬래그 및 플라이애시 만으로 설계기준압축강도 80MPa의 3성분계 고강도콘크리트(이하 고강도콘크리트)를 개발하기 위하여, 고로슬래그와 플라이애시의 대체율이 고강도콘크리트의 경화전 후 재료물성 변화에 미치는 영향을 평가하였다. 고강도콘크리트의 경화전후 재료물성 평가결과, 고로슬래그와 플라이애시 대체율이 최대 30%까지 증가할수록 유동성과 장기강도가 우수한 것으로 나타났다. 또한 OPC만으로 제작된 시험체와 비교하여 길이변화 특성이 우수하며, 혼화재 사용에 따른 탄산화는 없는 것으로 나타났다. 고강도콘크리트 재료물성 평가결과, 고로슬래그 대체율 25%, 플라이애시 대체율 15%일 경우, 경화전 후 재료물성이 가장 우수한 것으로 나타났다. 이 연구결과는 향후 고가의 실리카퓸을 대체할 수 있는 고강도콘크리트의 개발에 유용하게 활용될 수 있을 것으로 기대된다.