Analysis of mixing ratio of lacquer and glue for lacquer drying in low relative humidity environment

상온저습 환경에서의 옻의 건조를 위한 옻과 교의 배합 분석 연구

This study investigates the hardening characteristics of the mixture lacquer and glue at room temperature. Diverse samples were made from manufacturing of glue to the adding ratio in sap of the lacquer tree. After the examination of moisture content of samples, it has been seen that there is no relation with glue's kinds or adding ratio, but only with contain level of moisture. The samples made with film shape in order to examine the drying time. Samples with isinglass needed for over three days and had smooth surface. However, samples mixed with animal glue dried within a day and had ripples on the surface because of fast drying rate. In addition, the samples with isinglass had slow change of colour in early step of drying and no colour difference after completely drying although it had significant changes to black oxide as soon as contact with air. In structural analysis with FT-IR showed that the carbonyl bond increased in the samples of mixed with glue, compared to raw lacquer and treated lacquer.

본 연구에서는 옻과 교의 배합을 통한 옻의 상온경화에 관한 연구를 진행하였다. 이를 위하여 교의 제조부터 옻에 첨가하는 비율까지 여러 시편을 제작하여 실험하였다. 옻의 건조와 가장 연관이 깊은 시편의 수분함유량을 측정한 결과 교의 종류 및 제조비율에 관계없이 첨가비율이 증가할수록 수분함량이 증가한 것을 확인하였다. 건조 시간을 알아보기 위한 도막 시편에서 어교를 배합한 시편은 약 3일 이상의 건조시간을 소비하였으나 매끈한 표면 상태 그대로 건조되었고, 아교를 배합한 시편은 하루 이내에 완전건조 하였으나 빠른 경화속도로 인해 표면에 주름이 생성되었다. 또한 어교를 배합한 시편은 아교를 배합한 시편이 공기와 접촉하자마자 검게 산화되는 것에 비해 초기 색변화가 느리게 진행되었으나 완전건조 후에는 색도에 큰 차이가 없는 것으로 나타났다. FT-IR을 통한 시편의 구조 분석에서 옻에 교를 배합한 시편의 카르보닐 결합이 기존의 생칠, 정제칠에 비해 증가한 것을 확인하였다.