Abstract
We analyzed the basic characteristics and adsorption property of carbonized materials from thinning byproducts of major Korean wood species for evaluating as charcoal making raw material. Yield of charcoal was decreased with increasing the carbonization temperature for all wood species. Refining degrees was 9.0 at $400^{\circ}C$, 3.3~5.0 at $600^{\circ}C$ and 0 at $800^{\circ}C$, and was no difference among wood species. With increasing the carbonization temperature, the fixed carbon content was also increased, and charcoal from softwoods had more fixed carbon content than that from hardwoods. Specific surface area was increased with increasing the carbonization temperature, softwood charcoal had more specific surface area than that of hardwood. Pinus rigida showed the highest specific surface area. In formaldehyde removal by charcoal, some materials had highest at $600^{\circ}C$ and the others had highest at $800^{\circ}C$. Pinus koraiensis, Qurcus acutissima and MDF showed maximum formaldehyde removal ability at $600^{\circ}C$. Ethylene gas removal ability of charcoal was increased with increasing the carbonization temperature, and the charcoal from Pinus rigida and Robinia pseudoacacia had higher ethylene gas removal ability than the other species.
본 연구에서는 한국산 주요 수종의 간벌재 및 목질재료의 탄화물로의 개발을 위해 이들을 탄화하여 기본물성 및 흡착 특성을 분석하였다. 탄화수율은 모든 수종과 목질재료에서 탄화온도 상승과 함께 감소했다. 정련도는 $400^{\circ}C$에서는 9.0, $600^{\circ}C$에서는 3.3~5.0, $800^{\circ}C$에서는 0으로 나타났고, 수종 간 차이가 적은 것으로 나타냈다. 고정탄소량은 탄화온도가 상승함에 따라 증가하였으며, 수종 간은 침엽수재 탄화물이 활엽수재 탄화물 보다 높은 경향을 보였다. 비표면적은 탄화온도가 증가할수록 증가하였고, 수종 간 비표면적은 침엽수재가 활엽수재 탄화물보다 높게 나타났으며, 리기다소나무 탄화물이 733.9 $m^2$/g으로 가장 높은 비표면적을 나타내다. 포름알데히드 제거율은 탄화 온도 간에는 탄화온도가 증가할수록 높았으나 600과 $800^{\circ}C$ 사이에서는 $600^{\circ}C$가 높은 것과 $800^{\circ}C$가 높은 것이 공존해 나타났고, 수종 간은 잣나무, 졸참나무 및 MDF 탄화물이 $600^{\circ}C$에서 높은 제거율을 나타냈다. 에틸렌가스 제거율은 탄화온도가 증가할수록 높은 제거율을 나타났고, 수종 간에는 리기다소나무, 아카시나무 탄화물이 가장 높은 제거율을 나타낸다.