High Cyclic Fatigue Life and Fracture Behaviors of Shot-Peened Bearing Steel

쇼트피닝 처리를 한 베어링강의 고사이클 피로수명 및 파괴거동

  • Received : 2011.04.18
  • Accepted : 2011.06.03
  • Published : 2011.09.01
Download PDF
⟨ Previous Next ⟩

Abstract

Shot-peening effects on the fatigue behavior of bearing steel were investigated under the high cyclic loading. Hourglass shape specimens were made of bearing steel(JIS-SUJ2) for rotary bending fatigue tests. Two kinds of treatments were performed : a heat treatment and a shot-peened surface treatment after the heat treatment. The fracture surfaces of specimens were classified into two types of fracture mode : the surface fracture mode induced by a surface defect and the internal fracture mode induced by a nonmetallic inclusion. Inclusion depth and shape affected considerably the fatigue life. Shot-peening treatment improved much the fatigue life of the bearing steel under low and high levels of cyclic loads. Probabilistic-stress-life (P-S-N) curves were suggested for the reliable fatigue life estimation of the improved bearing steel.

쇼트피닝(shot-peening) 처리를 한 베어링강의 고사이클 피로거동을 연구하였다. 열처리한 베어링강(JISSUJ2) 시험편과 열처리 후 쇼트피닝 표면가공을 추가한 시험편을 사용해 회전굽힘피로시험을 수행하고 파단 된 시험편의 파면을 분석하였다. 시험편의 피로파괴는 표면 결함에서 비롯된 표면 파괴와, 내부의 비금속개 재물에서 비롯된 내부형 파괴의 두 종류로 발생하였다. 내부 파괴의 경우 비금속 개재물 주변에 어안(fisheye) 모양의 파괴양식이 관찰되었다. 개재물은 표면으로부터의 깊이와 형상에 따라 피로 수명에 큰 영향을 주었다. 쇼트피닝 가공을 한 베어링강은 저사이클 하중영역 및 고사이클 하중영역에서 모두 피로수명이 향상되었으며, 하중이 작아질수록 피로수명의 개선은 더욱 커졌다. 또한 2 모수 와이블(Weibull) 분포를 이용하여 베어링강의 확률-응력-수명 (P-S-N) 곡선을 구하여 신뢰도 높은 피로수명 예측을 하였다.

Keywords

References

  1. First International Conference Held as "Fatigue Life in the Gigacycle Regime," 1998 in Paris. The Second : "Fatigue in the very High Cycle Regime," 2001 in Vienna, the Third : "Very High Cycle Fatigue (VHCF- 3)," 2004 in Kyoto
  2. Murakami, Y., Kodama, S. and Konuma, S., 1989," Quantitative Evaluation of Effects of Non-Metallic Inclusions on Fatigue Strength of High Strength Steels," International Journal of Fatigue, Vol. 11, Issue 5, pp. 291-298. https://doi.org/10.1016/0142-1123(89)90054-6
  3. Murakami, Y., 2002, "Metal Fatigue:Effects of Small Defects and Nonmetallic Inclusions," Elsevier Science Ltd. UK.
  4. Nishijima, S. and Kanazawa, K., 1999, "Stepwise S- N Curve and Fish-Eye Failure in Gigacycle Fatigue ," Fatigue & Fracture of Engineering Materials & Structure,Vol. 22,Issue7, pp.601-607. https://doi.org/10.1046/j.1460-2695.1999.00206.x
  5. Shiozawa, K., Morii, Y., Nishino, S. and Lu, L., 2010, "Subsurface Crack Initiation and Propagation Mechanism in High-Strength Steel in a very High Cycle Fatigue Regime," International Journal of Fatigue, Vol. 28, Issue 11, pp.1521-1532.
  6. Sakai, T., Lian, B., Takeda, M., Shiozawa, L., Oguma, N., Ochi, Y., M Nakajima,. and Nakamura, T., 2010, "Statistical Duplex S-N Characteristics of High Carbon Chromium Bearing Steel in Rotating Bending in very High Cycle Regime," International Journal of Fatigue,Vol. 32, Issue 8-9, pp.765-773.
  7. Atkinson, H. V. and Shi, G., 2003, "Characterization of Inclusions in Clean Steels : A Review Including the Statistics of Extremes Methods," Progress in Materials Science, Vol. 48, Issue 5, pp.457-520. https://doi.org/10.1016/S0079-6425(02)00014-2
  8. Furuya, Y., Matsuoka, S., Abe, T. and Yamaguchi, K., 2002, "Gigacycle Fatigue Properties for High- Strength Low-Alloy Steel at 100 Hz, 600 Hz, and 20 kHz," Scripta Materialia, Vol. 46, Issue 2, pp. 157-162. https://doi.org/10.1016/S1359-6462(01)01213-1
  9. Tokaji, K., Itoga, H., Nakajima, M. and Ko, H. N., 2003, "Effect of Surface Roughness on Step-Wise S- N Characteristics in High Strength Steel," International Journal of Fatigue, Vol. 25, Issue 5, pp. 379-385. https://doi.org/10.1016/S0142-1123(02)00166-4
  10. Xenonphon, J.K., 1989, "Shot Peening Viable Method to Extending Component Life" SAE Technical Paper Series 891932, pp. 1-8
  11. Shiozawa, K. and Lu, L., 2002, "Very High-Cycle Fatigue Behaviour of Shot-Peened High-Carbon- Chromium Bearing Steel," Fatigue & Fracture of Engineering Materials & Structure, Vol. 25, Issue 8-9, pp.813-822. https://doi.org/10.1046/j.1460-2695.2002.00567.x
  12. Lee, T.S., Jang, J.H., Suh, C.M., Kim, J.H. and Kim, S.C., 2007, "Fatigue Characteristics of Bearing Steel n Giga Cycles" Transactions of the KSME(A), Vol. 31, No. 10, pp. 165-169.
  13. Cheng, S.-K., Lee, S.-H. and Chung, S.-C., 2001, "Effect of the Peening Intensity by Shot Peening," Transactions of the KSME(A), Vol. 25, No. 10, pp. 1590-1596.
  14. Kim, H.S. and Lee, S.H., 1998, "The Stress Distribution and Improvement of Fatigue Strength for Notched Materials by Shot Peening," Journal of the Korean Society of Machine Tool Engineers, Vol. 7, No. 5, pp. 120-126.
  15. JIS Z 2274, "Method of Rotating Bending Fatigue Testing of Metals."
  16. ASTM, 1994, "Standard Test Method for Determining The Effective Elastic Parameter for X-ray Diffraction Measurement of Residual Stress.," ASTM E 1426-94, pp.932-935
  17. KS B ISO 1143, "Metallic Materials - Rotating bar Bending Fatigue Testing."
  18. Shiozawa, K. and Lu, L., 2002, "Very High-Cycle Fatigue Behaviour of Shot-Peened High-Carbon- Chromium Bearing Steel," Fatigue&Fracture of Engineering Materials & Structure, Vol. 25, Issue 8-9, pp.813-822. https://doi.org/10.1046/j.1460-2695.2002.00567.x
  19. Li, W., Sakai, T., Li, Q., Lu, L.T. and Wang, P., 2010, "Reliability Evaluation on very High Cycle Fatigue Property of GCr15 Bearing Steel," International Journal of Fatigue, Vol. 32, Issue 7, pp.1096-1107. https://doi.org/10.1016/j.ijfatigue.2009.12.008
  20. Ravichandran, K.S., Ritchie, R.O. and Murakami, Y., 1999, "Small Fatigue Cracks : Mechanics, Mechanisms and Applications," Elsevier
  21. Sakai, T., Sato, Y. and Oguma, N., 2002, "Characteristic S-N Properties of High-Carbon- Chromium-Bearing Steel Under Axial Loading in Long-Life Fatigue," Fatigue & Fracture of Engineering Materials & Structures, Vol. 25, Issue 8-9, pp. 765-773. https://doi.org/10.1046/j.1460-2695.2002.00574.x
  22. Murakami, Y., Takada, M. and Toriyama, T., 1998, "Super-Long Life Tension-Compression Fatigue Properties of Quenched and Tempered 0.46% Carbon Steel," International Journal of Fatigue, Vol. 20, Issue 9, pp. 661-667. https://doi.org/10.1016/S0142-1123(98)00028-0
  23. Celik, A. and Karadeniz, S., 1995, "Improvement of the Fatigue Strength of AISI 4140 Steel by an Ion Nitriding Process," Surface and Coatings Technology, Vol. 72, Issue 3, pp. 169-173. https://doi.org/10.1016/0257-8972(94)02348-4
  24. Jung, D.W. and Choi, N.S., 2010, "Evaluation of Statistical Fatigue Life of Hybrid Composite Joints in Low-Floor Bus," Transactions of the KSME(A), Vol. 34, No. 11, pp. 1705-1714. https://doi.org/10.3795/KSME-A.2010.34.11.1705
  25. Park, D.C., 2001, "Electrical Engineering Probability," Intervision, Korea.

Cited by

  1. An investigation on the fatigue behavior of DCB specimen bonded with aluminum foam at Mode III vol.30, pp.10, 2016, https://doi.org/10.1007/s12206-016-0915-x
  2. A study on fracture behaviors of aluminum and CFRP jointed with pin vol.32, pp.8, 2018, https://doi.org/10.1007/s12206-018-0713-8