초록
티타늄합금 안경테 홈선을 제작하기 위한 냉간 압연 롤러를 설계하고 제작 후 그에 대한 성능 평가를 실시하였다. 롤러의 표면 거칠기 값은 $Ra=0.05-0.15{\mu}m$이고 $Rz=0.23-0.67{\mu}m$였다. 이 값은 티타늄안경테 PVD(Physical Vapor Deposition)도금을 위한 바렐 연마 후 측정한 표면 거칠기 값 $Ra=0.04{\mu}m$, $Rz=0.3{\mu}m$과 비교할 때 만족할만한 결과였다. Ti-3Al-2.5V(Half titanium)와이어를 냉간 압연한 결과 경도가 221Hv, 247Hv(1st), 270Hv(2nd)등으로 증가하므로 적절한 열처리와 다단압연공정이 필요함을 알 수 있었다.
After the design and production of cold rolling to make titanium-alloyed(Gr.9) eyerim, the function of the roller was evaluated. The surface roughness values of the roller of Ra was $0.05{\sim}0.156{\mu}m$ and of Rz was $0.23{\sim}067{\mu}m$. The values showed a satisfactory result compared with the surface roughness values Ra was $0.04{\mu}m$ and Rz was $0.3{\mu}m$ which was measured after barrel polishing for the titanium eyeglasses frame PVD (Physical Vapor Deposition) gilding. As a result of cold rolling of Ti-3Al-2.5V (Half Titanium), the degree of hardness increased to 221Hv, 247Hv(1st), 270Hv(2nd), etc. Therefore, it was found that proper heat treatment and multi-stand rolling process are necessary.