Properties on the Freeze-Thaw of Concrete Subjected to Seawater Attack

해수의 영향을 받은 콘크리트의 동결융해 특성

  • Received : 2010.03.25
  • Accepted : 2010.12.03
  • Published : 2011.02.28

Abstract

In this study, deterioration degrees of concrete were investigated at laboratory under seawater attack and cycling freeze-thaw, which are major durability performance deterioration factors of concrete. Deteriorations of mixed concrete using Portland & blended cement were examined by instrumental analysis of changes in relative dynamic modulus of elasticity and compressive strength. After 520 cycles of freeze-thaw, relative dynamic modulus of elasticity and compressive strength of concrete mixed with normal Portland and LHC over 75% showed relatively low resistance of approximately 44% of those values of SRC. Concrete replaced with 50% fine powder of blast furnace slag showed the most excellent freeze-thaw resistance among the tested blended cement concrete.

이 연구는 콘크리트의 내구성 저하요인인 해수침식 및 동결융해 반복작용을 받은 콘크리트의 성능저하 정도를 실험적으로 고찰하기 위하여 포틀랜드 및 혼합시멘트를 사용하여 콘크리트 공시체를 제조한 후 상대동탄성계수, 압축강도 변화 및 기기분석을 통하여 성능저하 원인을 구명하였다. 동결융해 520싸이클까지의 결과 보통포틀랜드 및 저열포틀랜드시멘트는 75% 이상의 상대동탄성계수와 압축강도가 내황산염포틀랜드시멘트 약 44%의 값을 나타내어 상대적으로 낮은 저항성을 나타내었으며, 고로슬래그미분말을 50% 대체하여 사용한 콘크리트가 혼합시멘트계 콘크리트 중 가장 우수한 동결융해 저항성을 나타내었다. 혼합시멘트계 콘크리트의 해수침식 유 무에 따라 비교한 결과, 고로슬래그미분말 콘크리트의 잠재수경성 촉진으로 동결융해 저항성이 우수하였으나, 실리카퓸을 혼합한 콘크리트는 해수침식에 의한 성능저하가 발생하여 동결융해 저항성이 낮아지는 경향을 나타내었고, 해수침식 및 동결융해 작용을 받은 보통포틀랜드 콘크리트는 동결융해 작용에 의한 쏘마싸이트 피크와 해수침식에 의한 석고 및 프리델 염분 피크가 주로 검출되고, 고로슬래그미분말을 혼합한 콘크리트는 해수침식의 유 무에 상관없이 좋은 결과를 나타내었다.

Keywords

References

  1. 문한영, 이승태, 김홍삼, 김성수, “화학적 침식을 받은 포틀랜드계 시멘트 모르타르의 저항성 평가,” 대한토목학회논문집, 22권, 1-A호, 2002, pp. 181-191.
  2. 문한영, 김성수, 김홍삼, 이승태, “시멘트 모르타르의 인공해수 침식에 대한 저항성,” 대한토목학회 학술발표회논문집(I), 2000, pp. 443-446.
  3. ASTM C 666, “Resistance of Concrete to Rapid Freezing and thawing,” In Annual Book of ASTM Standards, 1984.
  4. Sabir, B. B., “Mechanical Properties and Frost Resistance of Silica Fume Concrete,” Cement and Concrete Composite, Vol. 19, 1997, pp. 285-294. https://doi.org/10.1016/S0958-9465(97)00020-6
  5. Miao, C., Mu, R., Tian, Q., and Sun W., “Effect of Sulfate Solution on the Frost Resistance of Concrete with and without Steel Fiber Reinforcement,” Cement and Concrete Research, Vol. 32, 2002, pp. 31-34. https://doi.org/10.1016/S0008-8846(01)00624-X
  6. Sabir, B. B., “Mechanical Properties and Frost Resistance of Silica Fume Concrete,” Cement and Concrete Composite, Vol. 19, 1997, pp. 285-294. https://doi.org/10.1016/S0958-9465(97)00020-6
  7. Conjeaud, M. L., “Mechanism of Sea Water Attack on Cement Mortar,” Performance of Concrete in Marine Environment, ACI Publication SP-65, 1980, pp. 22-39.
  8. Antonio, C. and Julio, A., “Case Studies of Concrete Deterioration in a Marine Environment in Portugal,” Cement and Concrete Composite, Vol. 24, 2002, pp. 169-179. https://doi.org/10.1016/S0958-9465(01)00037-3
  9. Gjorv, O. E. and Kashino, N., “Durability of a 60-Year Old Reinforced Concrete Pier in Oslo Harbor,” Materials Performance, Vol. 25, No. 2, 1986, pp. 18-26.
  10. Harrison, W. H., “Effect of Chloride in Mix Ingredients on Sulphate Resistance of Concrete,” Magazine of Concrete Research, Vol. 42, No. 152, 1990, pp. 113-126. https://doi.org/10.1680/macr.1990.42.152.113
  11. Goni, S., Lorenzo, MaP., Sagrera, J. L., “Durability of Hydrated Portland Cement with Copper Slag Addition in $NaCl+Na_2SO_4$ Medium,” Cement and Concrete Research, Vol. 24, No. 8, 1994, pp. 1403-1412. https://doi.org/10.1016/0008-8846(94)90153-8
  12. Mehta, P. K., Concrete Structures, Properties and Materials, Prentice-Hall, Inc., New Jersey, 1993, 196 pp.

Cited by

  1. Resistance of concrete made with air- and water-cooled slag exposed to multi-deterioration environments vol.20, pp.3, 2018, https://doi.org/10.7855/IJHE.2018.20.3.011