Microstructure and mechanical properties in hot-forged liquid-phase-sintered silicon carbide

고온단조에 의한 액상소결 탄화규소의 미세구조 및 기계적 특성

Two kind of $\beta$-SiC powders of different particle sizes (${\sim}1.7\;{\mu}m$ and ${\sim}30\;nm$), containing 7 wt% $Y_2O_3$, 2 wt% $Al_2O_3$ and 1 wt% MgO as sintering additives, were prepared by hot pressing at $1800^{\circ}C$ for 1 h under applied pressures, and then were hot-forged at $1950^{\circ}C$ for 6 h under 40 MPa in argon. All the hot-pressed specimens consisted of equiaxed grains and were developed grain growth after hot-forging. The smaller starting powder was developed the finer microstructure. The microstructures on the surfaces parallel and perpendicular to the pressing direction of the hot-forged SiC were similar to each other, and no texture development was observed because of the lack of massive $\beta$ to $\sigma$ phase transformation of SiC. The fracture toughness (${\sim}3.9\;MPa{\cdot}m^{1/2}$), hardness (~ 25.2 GPa) and flexural strength (480 MPa) of hot-forged SiC using larger starting powder were higher than those of the other.

평균 입도의 크기가 ${\sim}1.7\;{\mu}m$와 ${\sim}30\;nm$인 두 종류의 탄화규소 분말을 7 wt% $Y_2O_3$, 2 wt% $Al_2O_3$, 1 wt% MgO를 소결 첨가제로 사용하여 $1800^{\circ}C$에서 1 시간동안 Ar 분위기에서 압력을 가하여 고온가압소결을 하였다. 고온 가압소결한 시편은 $1950^{\circ}C$에서 6 시간동안 Ar 분위기에서 40 MPa의 압력을 가하여 고온 단조 하였다. 두 시편 모두 고온가압소결 후의 미세구조는 등방형 모양의 결정립을 나타내었으며, 고온 단조 후에 결정립 성장이 나타났다. 평균 입도의 크기가 작은 탄화규소 분말로 소결한 시편의 결정립의 크기가 고온 단조 후에도 더 작은 결정립을 나타내었다. 고온 단조 후의 압력축과 평행한 방향과 수직한 방향의 미세구조는 비슷하였다. 탄화규소의 $\beta$에서 $\alpha$로의 상변태가 활발하게 발생하지 않아 집합조직의 발달은 발견되지 않았다. 평균 입도의 크기가 큰 탄화규소 분말로 제작된 시편의 파괴인성 (${\sim}3.9\;MPa{\cdot}m^{1/2}$), 경도 (~ 25.2 GPa), 굽힘강도가 (480 MPa) 평균 입도의 크기가 작은 탄화규소로 제작된 시편보다 높게 나타났다.