Spalling Properties of 60, 80MPa High Strength Concrete with Fiber

복합섬유(PP, NY)를 혼입한 60, 80MPa 3성분계 고강도콘크리트의 내화특성

  • Kim, Seong-Deok (Construction Technology Reserch Dept., Land & Housing Institute) ;
  • Kim, Sang-Yun (Construction Technology Reserch Dept., Land & Housing Institute) ;
  • Bae, Ki-Sun (Construction Technology Reserch Dept., Land & Housing Institute) ;
  • Park, Su-Hee (Construction Technology Reserch Dept., Land & Housing Institute) ;
  • Lee, Bum-Sik (Construction Technology Reserch Dept., Land & Housing Institute)
  • Received : 2010.02.08
  • Accepted : 2010.05.05
  • Published : 2010.08.20

Abstract

Fire resistance and material properties of high-strength concrete (W/B 21.5%, 28.5%) with OPC, BS and FA were tested in this study. Main factors of the test consisted of fiber mixing ratio and W/B. Two types of fiber (NY, PP) mixed with the same weight were used for the test. The fiber mixing ratios were 0%, 0.05%, 0.1%, and 0.2% of the concrete weight. After performing the test, Under the W/B level of 21.5% and 28.5%, the spalling was effectively resisted by using the high strength concrete with fiber mixing ratios of 0.05%~0.1%. Compressive strength, flowability and air content are similar those of the fiberless high-strength concrete with the same W/B.

본 연구는 고강도콘크리트의 내화성능 증진에 효과적인 것으로 알려진 섬유(PP+NY) 혼입율 변화에 따른 60 MPa, 80 MPa 3성분계 고강도콘크리트의 유동성 및 강도특성을 검토하고 내화시험을 통해 폭렬현상을 확인하였다. 섬유(PP+NY) 혼입율을 0%, 0.05%, 0.1%, 0.2%로 산정하여 실험한 결과, 유동성 및 강도가 미세하지만 저하하는 것으로 나타났으나, 전반적으로 목표 범위를 만족하는 것으로 나타났다. 3시간 내화 후 폭렬특성으로 0%에서는 폭렬현상이 나타났지만, 0.05%이상에서는 표면에 미세한 균열만 발생하고 피복 탈락현상은 나타나지 않는 것으로 나타났다. 또한 폭렬이 발생되지 않은 공시체의 경우 잔존압축강도율이 5 ~ 6%로 나타났다. 이상 적은 양의 섬유(PP+NY)혼입율인 0.05%이상에서 폭렬현상이 방지되어 가장 양호한 것으로 판단된다.

Keywords

References

  1. Kim HY, Seo CH, An Experimental Study on the Physical Properties by Compressive Strength Areas of Concrete at High Temperature, Journal of the Architectural Institute of Korea (Structure & Construction), 2004;20(11):75-82.
  2. Han CG, Yang SH, Han MC, Pei CC, The Influence of Polymer Contents and Appearance on Spalling Prevention of High Strength Concrete, Journal of the Architectural Institute of Korea (Structure & Construction), 2009;24(5):93-100.
  3. Na CS, Shin SB, Cho BS, Kwon YJ, Kim GY, Kim MH, An Experimental Study on the Explosive Spalling Properties of High Performance Concrete by Material Factors, Annual Conference of the Architectural Institute of Korea, 2006:357-360.
  4. Song H, Chu YS, Lee JK, Strength and Deformation iof High Strength Concrete in High Temperatures, Proceeding of Conference in Architectural Institute of Korea, 2006:505-508.
  5. Sin SW, Yu SH, Kim YK, Spalling Reduction Methods of Ultra High-Strength Reinforced Concrete Columns , Journal of the Korea institute for Structural Maintenance Inspection, 2006;10(5):171-178.
  6. J.G. Sanjayan, Design against spalling of concrete in fire, Proceeding of the First Korea-Australia Workshop on Recent Advance in high Performance Concrete, 2005:155-169.
  7. K.D. Hertz, Limits of spalling of fire-exposed concrete, Fire Safety Journal 2003;38:103-116. https://doi.org/10.1016/S0379-7112(02)00051-6
  8. Han CG, Yang SH, Lee BY, Hwang YS, A Study on the Spalling Properties of High-Performance Concrete with the Kinds of Aggregate and Polypropylene Fiber Contents, Journal of the Korea Concrete Institute 1999;11(5):69-77.
  9. Han CG, Kim SS, Kim SS, Pei CC, Spalling Prevention of High Strength Concrete Due to Hybrid Organic Fiber and Different Lengths of Polypropylene Fibers, Journal of the Architectural Institute of Korea (Structure & Construction), 2008;24(2):61-68.
  10. Choi SM, Lee BS, Bae KS, Kim SY, Park SH; Rheological Characteristics of Fiber-Reinforced High-Strength AFR Concrete, Proceedings of the Korea Concrete Institute 2009:543-544.