Abstract
In this study, the performance improvement of epoxy resin system had been tried by the improvement of particle size distribution and globularization of filler using polymerization method. From the results of particle size distribution measurement, the polydispersity value of reformed filler was 1.04 and that of silica flour before reformation was 2.6, it could be confirmed that the particle size uniformity of reformed filler had been improved greatly and the shape of particle was globular. Compatibility between monomer and silica was improved remarkably with the silanization pretreatment of silica flour. From the results of degree of crosslinking test, it could be confirmed that the binding structure of reformed filler was 3-dimensional net structure. And it could be also confirmed that the fluidness was improved at the casting of epoxy resin with reformed filler. From the above results, it could be concluded that the reformation of filler with the improvement of particle size distribution and globularization was very successful method to improve the performance of cast epoxy resin system.
본 연구에서는 고분자중합방법을 이용한 충진제 입도개선 및 구형화를 통해 충진제를 개질함으로써 에폭시복합체의 성능향상을 도모하였다. 개질된 충진제의 입도분포의 측정 결과 고분자비드의 PD(Polydispersity)값이 1.04로 개질전 충진제인 실리카 분말의 PD값 2.6에 비해 입자의 균일도가 상당히 개선된 결과를 가져왔으며 입도의 형태도 구형상을 유지하고 있음을 확인하였다. 실리카에 대한 실란전처리를 실시한 결과 모노머와 실리카의 상용성이 대폭 향상 되는 것을 확인하였으며 가교도 측정 결과 개질된 충진제가 3차원 망상구조를 지니고 있음을 확인할 수 있었다. 에폭시복합체의 성형시 충진제로 인한 유동성의 변화를 측정한 결과, 유동성이 향상됨을 확인하였다. 이상의 결과를 바탕으로 입도분포 개선 및 구형화를 통한 충진제 개질이 에폭시복합체 성능개선을 위한 매우 유용한 방법임을 확인하였다.