알칼리 표면개질을 통한 메조포러스 알루미늄 하이드록사이드 필름 형성 기구

Formation Mechanism of Mesoporous Aluminum Hydroxide Film by Alkali Surface Modification

  • 서영익 (한양대학교 신소재공학부) ;
  • 전용진 (한양대학교 신소재공학부) ;
  • 이영중 (한양대학교 신소재공학부) ;
  • 김대건 (한양대학교 신소재공학부) ;
  • 이규환 (한국과학기술연구원) ;
  • 김영도 (한양대학교 신소재공학부)
  • Seo, Young-Ik (Division of Materials Science and Engineering, Hanyang University) ;
  • Jeon, Yong-Jin (Division of Materials Science and Engineering, Hanyang University) ;
  • Lee, Young-Jung (Division of Materials Science and Engineering, Hanyang University) ;
  • Kim, Dae-Gun (Division of Materials Science and Engineering, Hanyang University) ;
  • Lee, Kyu-Hwan (Computational Science Center, Korea Institute of Science and Technology) ;
  • Kim, Young-Do (Division of Materials Science and Engineering, Hanyang University)
  • 발행 : 2010.02.27

초록

In this study, a new, relatively simple fabrication method for forming a mesoporous $Al(OH)_3$ film on Al substrates was demonstrated. This method, i.e., alkali surface modification, was simply comprised of dipping the substrate in a $5\times10^{-3}$ M NaOH solution at $80^{\circ}C$ for one minute and then immersing it in boiling water for 30 minutes. After alkali surface modification, a mesoporous $Al(OH)_3$ film was formed on the Al substrate, and its chemical state and crystal structure were confirmed by XPS and TEM. According to the results of the XPS analysis, the flake-like morphology after the alkali surface modification was mainly composed of $Al(OH)_3$, with a small amount of $Al_2O_3$. The mesoporous $Al(OH)_3$ layer was composed of three regions: an amorphousrich region, a region of mixed amorphous and crystal domains, and a crystalline-rich region near the $Al(OH)_3$ layer surface. It was confirmed that the stabilization process in the alkali surface modification strongly influenced the crystallization of the mesoporous $Al(OH)_3$ layer.

키워드

참고문헌

  1. J. Chen, S. Truesdail, F. Lu, G. Zhang, C. Belvin, B.Koopman, S. Farrah and D. Shah, Water Res., 32(7),2171(1998). https://doi.org/10.1016/S0043-1354(97)00427-2
  2. S. Goldberg, J. A. Davis, and J. D. Hem, The EnvironmentalChemistry of Aluminum, 2nd ed., p. 271, LewisPublishers, New York, U.S.A., (1996).
  3. H. Liu, J. S. Tse, J. Hu, Z. Liu, L. Wang, J. Chen, D. J.Weidner, Y. Meng, D. Hausemann and H. -K. Mao, J.Phys. Chem. B 109(18), 8857 (2005). https://doi.org/10.1021/jp0501594
  4. R. Demichelis, Y. Noel, B. Civalleri, C. Roetti, M. Ferrero and R. Dovesi, J. Phys. Chem. B 111(31), 9337 (2007). https://doi.org/10.1021/jp072501d
  5. J. -F. Chen, L. Shao, F. Guo and X. -M. Wang, Chem.Eng. Sci. 58(3-6), 569 (2003). https://doi.org/10.1016/S0009-2509(02)00581-X
  6. K. J. Bayer, Patent DE-PS 43977 (1887).
  7. J. Bhom, Z. Anorg. Allg. Chem. 149, 203 (1925). https://doi.org/10.1002/zaac.19251490114
  8. C. Dewey, Am. J. Sci. 2, 249 (1820).
  9. R. A. V. Nordstrand, W. P. Hettinger and C. D. Keith, Nature 177(4511), 713 (1956). https://doi.org/10.1038/177713a0
  10. G. Y. Chao, J. Baker, A. P. Sabina and A. C. Roberts, Can.Miner. 23, 21 (1985).
  11. R. Demichelis, B. Civalleri, Y. Noel, A. Meyer and R.Dovesi, Chem, Phys. Lett. 465(4-6), 220 (2008).
  12. Y. Cesteros, P. Salagre, F. Medina and J.E. Sueiras, Chem.Mater. 13(8), 2595 (2001). https://doi.org/10.1021/cm011007y
  13. Y. H. Oh, C. K. Rhee, D. H. Kim, G. H. Lee and W. W.Kim, J. Mater. Sci. 41(13), 4191 (2006). https://doi.org/10.1007/s10853-006-6988-7
  14. Y. Lee, Y. Liu and C. -S. Yeh, Phys. Chem. Chem. Phys.1(19), 4681 (1999). https://doi.org/10.1039/a905178c
  15. Y. I. Seo, D. -G. Kim, Y. D. Kim, B. J. Lee and K. H. Lee, Scripta Mater. 59(8), 889 (2008). https://doi.org/10.1016/j.scriptamat.2008.06.049
  16. J. F. Moulder, W. F. Stickle, P. E. Sobol and K. D.Bomben, Handbook of X-ray Photoelectron Spectroscopy, p. 213, Physical Electronics, Inc., Eden Prarie, MN,U.S.A., (1995).
  17. K. Wefer sand C.Misra, Oxides and hydroxides of aluminum, Technical Paper No. 19, Aluminum Company of America, Pittsburgh, PA, (1987)
  18. J. S. C. Loh, A. M. Fogg, H. R. Watling, G. M. Parkinson and D. O'Hare, Phys. Chem. Chem. Phys. 2(16), 3597 (2000). https://doi.org/10.1039/b003050n
  19. G. C. Bye and J. Robbinson, Kolloid Z. Z. Polymere 198, 53 (1964). https://doi.org/10.1007/BF01499454
  20. H. Ginsberg, W. Huttig and H. Stiehl, Z. Anorg. Alg. Chem. 318, 238 (1962). https://doi.org/10.1002/zaac.19623180503

피인용 문헌

  1. Application of brass scrubber filter with copper hydroxide nanocomposite structure for phosphate removal vol.20, pp.2, 2015, https://doi.org/10.4491/eer.2014.062