Abstract
In this paper an experimental program was launched to determine the mechanical and durability properties of spall repair materials (RCC: 3 items, PCC: 2 items, PC: 3 items). Test items were mechanical property tests such as setting times, strengths, modulus of elasticity, plastic shrinkage, and durability tests such as dynamic modulus ratio, bond property with freeze-thaw, water absorption, chemical resistance, ultraviolet exposure. Modulus of the PC products exhibits ductile while the modulus is in the order of RCC > PCC > PC. At early ages the PC products experience higher plastic shrinkage than others, henceforth stable at 28 days. Other test results such as dynamic modulus ratio, absorption, and chemical resistance show that the PCs are superior to the PCCs and the RCCs. Except for PC-2, all patch materials had bond strength more than 1.3MPa after freeze-thaw cycles of 200~300 while the PCs and the PCCs seem to be better than the RCCs. With 500 hours of ultraviolet exposure, all patch materials showed to have no crack or deterioration at the surface.
본 연구에서는 콘크리트포장의 단면보수용 복합재료 8개(초속경시멘트계열 : RCC 3종, 폴리머시멘트계열 : PCC 2종, 폴리머계열 : PC 3종)에 대해 역학적인 특성 및 내구성 실험을 수행하였다. 역학적 특성으로서 응결시간, 압축강도, 휨강도, 탄성계수, 경화수축에 대해 실험하였고, 내구성으로서 동탄성계수 및 동결융해 후 부착강도, 흡수율, 내화학성, 자외선 노출 실험을 수행하였다. 탄성계수는 RCC>PCC>PC계열의 순으로 나타나서 폴리머가 사용되면서 연성의 특성을 보였다. 초기 재령에서의 폴리머 콘크리트의 경화수축이 상대적으로 큰 것으로 관찰되었지만 재령 28일에서는 다소 안정된 결과를 보였다. 상대동탄성계수, 흡수율, 10% $CaCl_2$와 10% $Na_2SO_4$의 화학용액을 사용한 내화학성 실험결과 PC계열, PCC계열, RCC계열 순으로 저항성이 우수한 것으로 나타났다. 200~300회 동결융해 이후의 부착강도 실험결과 PC-2를 제외하고는 모두 1.3MPa 이상을 확보하였고, PC 및 PCC 제품의 부착강도가 RCC 제품보다 전체적인 면에서 우수한 것으로 나타났다. 또한 시편을 500시간동안 자외선 노출시험 결과 모든 패치재료 시편에서 균열 및 표면 결함 등이 발견되지 않아 PC 및 PCC 제품의 자외선에 대한 내구성이 확보됨을 확인하였다.