Engineering Characteristics Analysis of High Strength Concrete Followed in replacement ratio increase in Blast Furnace Slag

고로슬래그 미분말의 치환율 증가에 따른 고강도 콘크리트의 공학적 특성 분석

This research examined engineering properties of high performance concrete, when substitution rate of BS increases. A summary of the test result is as follows. The fluidity of unset concrete increases as the substitution rate of BS increases. The amount of air is reduced more or less, but it seems that enough amount of air can be secured by using more air-entraining agent. Setting time is dramatically delayed as the substitution rate of BS increases. The compressive strength of hardening concrete was weaker than OPC before 28 days passes, due to latent hydraulic property of BS. However, after 28 days, it shows same or better property, which is exceptional for the practical uses of hyper strength concrete. Changes in drying shrinkage rate is quite much, because when hydration happens, the amount of free water in concrete increased as W/B gets larger. The amount of drying shrinkage increases as BS substitution rate increases, but every composition shows less than $-500{\times}10^{-6}$, which is relatively fine.

본 연구는 BFS치환율 증가에 따른 고강도 콘크리트의 제반 공학적 특성을 검토하였는데, 그 결과를 요약하면 다음과 같다. 굳지않은 콘크리트의 유동성은 BFS 치환율이 증가할수록 증가하는 경향을 나타내었고, 공기량은 다소 감소하는 경향을 나타내었으나 AE제 사용량 증가로 적정량의 공기량 확보는 가능할 것으로 판단된다. 응결시간은 BFS 치환율이 증가할수록 비례적으로 크게 지연되는 것으로 나타났다. 경화 콘크리트의 압축강도는 BFS의 잠재수경성 반응에 기인하여 BFS 치환율이 증가할수록 재령 28일 미만에서는 OPC에 비하여 저하하였으나, 그 이후 재령에서는 동등 이상의 수준을 발휘 하는 것으로 나타나 특히, 고강도 콘크리트의 활용에 탁월한 효과가 있는 것으로 분석되었다. 건조수축길이 변화율은 W/B가 클수록 수화반응시 콘크리트 내부에 존재하는 자유수의 양이 증가함에 기인하여 다소 크게 나타났고, BFS 치환율이 증가할수록 건조수축량은 증가하는 경향이 나타났으나, 모든 배합에서 $-500{\times}10^{-6}$이하로 비교적 양호하였다.