TiN/Ti 다층막 코팅된 생체용 Ti-30Ta-xZr 합금의 부식특성

Corrosion Characteristics of TiN/Ti Multilayer Coated Ti-30Ta-xZr Alloy for Biomaterials

  • 김영운 (전남대학교 치의학전문대학원 보철과) ;
  • 조주영 (조선대학교 치과대학 치과재료학교실) ;
  • 최한철 (조선대학교 치과대학 치과재료학교실)
  • Kim, Y.U. (Department of Dental Science, Chonnam National University, Graduate School) ;
  • Cho, J.Y. (Department of Dental Materials & Research Center of Nano-Interface Activation for Biomaterials, School of Dentistry, Chosun University) ;
  • Choe, H.C. (Department of Dental Materials & Research Center of Nano-Interface Activation for Biomaterials, School of Dentistry, Chosun University)
  • 투고 : 2009.07.08
  • 심사 : 2009.07.31
  • 발행 : 2009.08.01

초록

Pure titanium and its alloys are drastically used in implant materials due to their excellent mechanical properties, high corrosion resistance and good biocompatibility. However, the widely used Ti-6Al-4V is found to release toxic ions (Al and V) into the body, leading to undesirable long-term effects. Ti-6Al-4V has much higher elastic modulus than cortical bone. Therefore, titanium alloys with low elastic modulus have been developed as biomaterials to minimize stress shielding. For this reason, Ti-30Ta-xZr alloy systems have been studied in this study. The Ti-30Ta containing Zr(5, 10 and 15 wt%) were 10 times melted to improve chemical homogeneity by using a vacuum furnace and then homogenized for 24 hrs at $1000^{\circ}C$. The specimens were cut and polished for corrosion test and Ti coating and then coated with TiN, respectively, by using DC magnetron sputtering method. The analyses of coated surface were carried out by field emission scanning electron microscope(FE-SEM). The electrochemical characteristics were examined using potentiodynamic (- 1500 mV~+ 2000 mV) and AC impedance spectroscopy(100 kHz~10 mHz) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The equiaxed structure was changed to needle-like structure with increasing Zr content. The surface defects and structures were covered with TiN/Ti coated layer. From the polarization behavior in 0.9% NaCl solution, The corrosion current density of Ti-30Ta-xZr alloys decreased as Zr content increased, whereas, the corrosion potential of Ti-30Ta-xZr alloys increased as Zr content increased. The corrosion resistance of TiN/Ti-coated Ti-30Ta-xZr alloys were higher than that of the TiN-coated Ti-30Ta-xZr alloys. From the AC impedance in 0.9% NaCl solution, polarization resistance($R_p$) value of TiN/Ti coated Ti-30Ta-xZr alloys showed higher than that of TiN-coated Ti-30Ta-xZr alloys.

키워드

참고문헌

  1. Y. Okazaki, M. Ohota, Y. Ito, and T. Tateishi, J. Japan Inst Metals, 59, 229 (1995) https://doi.org/10.2320/jinstmet1952.59.2_229
  2. J. A. Davidson and P. Kovacks, New Biocompatible, Low Modulus Titanium Alloy for Medical Implant, U.S. Patent no. 5, 169, 597 (1992)
  3. P. O. Ganrot, Environ. Health Perspect, 65, 363 (1986) https://doi.org/10.2307/3430204
  4. S. Ghosh, A. STirma, and G. Talukder, Biol Trace Elem Res, 35, 247 (1992) https://doi.org/10.1007/BF02783770
  5. B. D. Boyan, T. W. Hummert, D. D. Dean, and Z. Schwartz, Biomaterials, 17, 137 (1996) https://doi.org/10.1016/0142-9612(96)85758-9
  6. K. Wang, Mater. Sci Eng, A 213, 134 (1996) https://doi.org/10.1016/0921-5093(96)10243-4
  7. I. Dion, X. Rogues, N. More, L. Larousse, J. Caix, F. Lefebvre, F. Rouais, J. Gautreau, and C.H. Baguey, Biomaterials, 14, 712 (1993) https://doi.org/10.1016/0142-9612(93)90070-I
  8. W. G. Kim, H. C. Choe, Y. M. Ko, and W. A. Brantley, Thin Solid Films, 517, 5033 (2009) https://doi.org/10.1016/j.tsf.2009.03.165
  9. W. G. Kim, H. C. Choe, and Y. M. Ko, J. Kor. Phys. Soc., 54, 1036 (2009) https://doi.org/10.3938/jkps.54.1036
  10. D. M. Brunette, P. Tengvall, M. Textoe, and P. Thomsen, Titanium in Medicine, p. 299, Springer, New York, 2001
  11. B. N. Chapman, Glow Discharge Processes, p. 123, Jhon Wiley & Sons, New York, 1980
  12. L. A. Cyster, D. M. Grant, K. G. Parker, and T. L. Parker, Biomolecular Engineering, 19, 171 (2002) https://doi.org/10.1016/S1389-0344(02)00021-7
  13. M. Y. Oh, W. G. Kim, H. C. Choe, and Y. M. Ko, Corrosion Science and Technology, 8, 89 (2009)
  14. J. E. G Gonzalez and J. C. Mirza-Rosca, J Electro Chemi, 471, 109 (1999) https://doi.org/10.1016/S0022-0728(99)00260-0
  15. E. Kobayashi, T. J. Wang, H. Doi, T. Yoneyama, and H. Timanaka, Mater Sci:Mater Med, 9, 567 (1998) https://doi.org/10.1023/A:1008909408948
  16. A. K. Shukla, R. Balasubramaniam, and S, Bhargava, Intermetallics, 13, 631 (2005) https://doi.org/10.1016/j.intermet.2004.10.001